采用包混工艺合成了核壳结构的先驱体粉体,并引入一定量Al2O3、SiO2和Y2O3复合添加剂,通过成型、炭化和烧结工艺制备了多孔碳化硅陶瓷;分析了样品的物相、表面形貌、孔隙率、热导率、热膨胀系数、抗弯强度和抗热震性能.结果表明,在较低的烧结温度下制得了多孔碳化硅陶瓷,在1650℃烧结的多孔碳化硅陶瓷综合性能较好.
参考文献
| [1] | 魏雄武,杜传进.柴油机微粒捕集器关键技术发展现状与分析[J].柴油机设计与制造,2005(04):4-7. |
| [2] | Jihong She;Jian-Feng Yang;Naoki Kondo;Tatsuki Ohji;Shuzo Kanzaki;Zhen-Yan Deng .High-strength porous silicon carbide ceramics by an oxidation-bonding technique[J].Journal of the American Ceramic Society,2002(11):2852-2854. |
| [3] | 章林,曲选辉,段柏华,何新波.SiC多孔陶瓷的研究进展[J].粉末冶金技术,2007(02):139-144. |
| [4] | Wang C;Wang J;Park C B et al.Cross-linking behavior of a polysiloxane in preceramic foam processing[J].Journal of Materials Science,2004,39(15):4913. |
| [5] | Shi Limin;Zhao Hongsheng;Yan Yinghui et al.Fabrication of high purity porous SiC ceramics using coat mix process[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2007,460-461:645. |
| [6] | 杨阳;赵宏生;刘中国 等.一种高抗热震性多孔碳化硅陶瓷的制备方法[P].中国,2010101525494,2010-04-19. |
| [7] | 时利民 .基于包混工艺的多孔碳化硅陶瓷的制备与性能研究[D].北京:清华大学,2007. |
| [8] | 刘培生;马晓明.多孔陶瓷检测方法[M].北京:冶金工业出版社,2006 |
| [9] | N. Kanetake;M. Kobashi .Innovative Processing of Porous and Cellular Materials by Chemical Reaction[J].Scripta materialia,2006(4):521-525. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%