利用OM,SEM和TEM及ThermoCalc(TCFE 3数据库)热力学计算等方法,结合热稳定性试验数据,研究了两种不同铬含量的热作模具钢4Cr3SiWMoVNb钢和4Cr5SiWMoVNb钢的热稳定性能.结果表明:4Cr3SiWMoVNb钢和4Cr5SiWMoVNb钢的最佳淬火温度分别为1000℃和1030 C;回火温度高于600℃后,4Cr3SiWMoVNb钢表现出更好的回火抗性;随回火时间的延长,两钢的硬度均呈下降趋势,4Cr5SiWMoVNb钢中有较多的以含Cr为主的M23C6碳化物粗化长大,组织较快发生回复与再结晶,硬度下降较快,而4Cr3SiWMoVNb钢热稳定性相对优异.
参考文献
| [1] | 李平安;高军 .热作模具钢的热稳定性研究[J].金属热处理,1997,22(12):10-12. |
| [2] | Hisao Kamiya;Norioki Uehara .Influence of chromium on the tempering characteristics of hot-work die steels[J].Denki Seiko (Electric Furnace Steel),1979,50(03):173-180. |
| [3] | Koh-ichi Sudoh .Influence of C,Si,Mn,Cr,Mo and V on the characteristics of 5 % Cr hot-work die steel[J].Denki Seiko (Electric Furnace Steel),1989,60(04):367-375. |
| [4] | Odd Sandberg;Bengt Klarenfjord;Patricia Miller.Comparison of premium quality H13 and modified hot work die steel[J].Die Casting Engineer,2002(03):40-49. |
| [5] | Lars-ake Norstrom;Lennart Jonson.New premium die steel for the 1990s[J].Die Casting Engineer,1988(13):12-14. |
| [6] | 陈英伟,吴晓春,宋雯雯,闵永安.含铌热作模具钢中碳化物的演变对热稳定性的影响[J].材料热处理学报,2010(05):75-80. |
| [7] | 上海市机械制造工艺研究所.金相分析技术[M].上海:上海科学技术文献出版社,1987 |
| [8] | 宋维锡.金属学[M].北京:冶金工业出版社,1980 |
| [9] | 石楠楠,吴晓春,闵娜.4Cr2Mo2W2V钢中碳化物的演变对热稳定性的影响[J].材料热处理学报,2011(11):68-72. |
| [10] | Delagnes D;Lamesle P;Mathon MH;Mebarki N;Levaillant C .Influence of silicon content on the precipitation of secondary carbides and fatigue properties of a 5%Cr tempered martensitic steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):435-444. |
| [11] | 陈再枝;蓝德年.模具钢手册[M].北京:冶金工业出版社,2002 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%