研制的材料在650℃晶化得到40％的云母晶体(其余为玻璃相)时,弯曲强度为150MPa,可在高速车削条件下形成连续的带状切屑,第一次在普通车削条件下使脆性的玻璃陶瓷材料表现出延性的材料去除模式.试验结果表明,脆性材料的延性切削模式的实现是由于云母晶体对裂纹走向的引导和玻璃相的强烈的剪切变形能力的共同作用.切削后,可在750℃再次晶化,随晶体体积份数的增加,弯曲强度提高到210MPa.
By optimizing the composition and microstructure, a new mica glass-ceramic with excellent machinability
was obtained. For this kind of mica glass-ceramic, a continuous band chips can be formed in machining at a high velocity and cut depth after
crystallizing at 650℃ and containing 40vol% of mica crystals (the rest is a glass phase), while the flexible strength reaches to 150MPa.
The test results show that the mechanism of ductile-mode material removal of the brittle material is attributed to a combination of mica crystal
guidance for crack propagation and the ability of glass phase to produce intense shearing strain. The further crystallizing at 750℃ can
enhance the flexible strength to 210MPa with increasing the amount of crystalline phase after cutting.
参考文献
| [1] | Baik S. J. Am. Ceram. Soc., 1995, 78 (6): 1217--1222. [2] Hoche T, Habelitz S, Avramov I. Acta Mater., 1999, 47 (3): 735--744. [3] 程慷果, 万菊林, 梁开明(CHENG Kang-Guo, et al). 硅酸盐学报(Journal of Chinese Ceramic Society), 1998, 26 (3): 403--406. [4] Baik D S, No K S, Chun J S. Journal of Materials Science, 1995, 30: 1801--1806. [5] Ngoi B K A, Sreejith P S. Inter. J. Adv. Manu. Tech., 2000, 16: 547--550. [6] Sang-soon Ku, Gary Larsen, Sabri Cetinkunt. Mechatronics, 1998, 8: 381--393. [7] 福格尔著, 谢于深译. 玻璃化学, 第一版. 北京: 轻工业出版社, 1988. 346--358. [8] Lei S T, Shin Y C, Incropera F P. Int. J. Mach. Tool Manu., 2000, 40: 213--2233. [9] Pei Z J, Ferreira P M. Int. J. Mach. Tool Manu., 1998, 38: 1399--1418. [10] Samuel R S. Modern Glass Practice, the first edition. Boston: Ceramic Industry publishing company, 1975. 190--192. [11] Varadarajan A S, Philip P K, Ramamoorthy B. Int. J. Mach. Tool Manu., 2002, 42: 193--200. [12] 乌而曼D R, 克赖多N J主编, 王西成, 粱淑妍译. 玻璃的弹性与强度, 第一版. 北京: 轻工业出版社, 1988. 109--112. |