以富勒烯烟灰萃余物(DFS)为前驱体,CO2为活化剂,制备出高比表面积纳米级颗粒炭(ADFS)。采用TEM、XRD、氮气吸附技术对材料进行结构表征。研究产品作为电化学电容器电极材料的性能,考察制备工艺及条件对材料性能的影响。结果表明:活化温度和时间是影响产品比表面积和孔结构的主要因素。 ADFS作为电化学电容器电极材料表现出理想的双电层性能和优异的快速充放电性能:经1173 K,CO2活化2 h的样品,在400 mV·s-1扫描速率下,循环伏安曲线依然表现为准矩形特性,在4 A·g-1的电流密度下材料的质量比电容为126 F·g-1。
Activated carbons (ACs) were prepared by CO2 activation using depleted fullerene soot as precursor. The structure of the ACs was investigated by TEM, XRD, and nitrogen adsorption. Their electrochemical properties in electrochemical capacitors were tested by cyclic voltammetry (CV) and galvanostatic charge/discharge methods in a three-electrode cell. Activation temperature and time were proved to be key parameters in controling the development of porosity and surface area of the ACs. The ACs have an excellent electro-chemical performance with fast charge/discharge characteristics. AC activated at 1173 K for 2 h exhibits an excellent electrochemical per-formance even at a high scanning rate of 400 mV·s-1 with a quasi-rectangular CV curve and its specific capacitance is up to 126 F·g-1 at a high current density of 4 A·g-1 .
参考文献
[1] | Conway B E .Transition from"Supercapacitor” to"Battery” behav-ior in electrochemical energy storage[J].Journal of the Electrochemical Society,1991,138(06):1539-1548. |
[2] | PATRICE SIMON;YURY GOGOTSI .Materials for electrochemical capacitors[J].Nature materials,2008(11):845-854. |
[3] | Yanwu Zhu;Shanthi Murali;Meryl D. Stoller;K. J. Ganesh;Weiwei Cai;Paulo J. Ferreira;Adam Pirkle;Robert M. Wallace;Katie A. Cychosz;Matthias Thommes;Dong Su;Eric A. Stach;Rodney S. Ruoff .Carbon-Based Supercapacitors Produced by Activation of Graphene[J].Science,2011(Jun.24 TN.6037):1537-1541. |
[4] | 郑冬芳,贾梦秋,徐斌,张浩,曹高萍,杨裕生.高性能超级电容器用高比表面积、层次孔结构炭材料的简便制备[J].新型炭材料,2013(02):151-155. |
[5] | A. G. Pandolfe;A. F. Hollenkamp .Carbon properties and their role in supercapacitors[J].Journal of Power Sources,2006(1):11-27. |
[6] | Chang Liu;Feng Li;Lai-Peng Ma;Hui-Ming Cheng .Advanced Materials for Energy Storage[J].Advanced Materials,2010(8):E28-E62. |
[7] | 李航,张明明,邢路阳,肖正浩,许钦一,周颖.富勒烯烟灰的研究进展[J].炭素技术,2009(04):35-40. |
[8] | Jieshan Qiu;Gang Chen;Zhentao Li .Preparation of double-walled carbon nanotubes from fullerene waste soot by arc-discharge[J].Carbon: An International Journal Sponsored by the American Carbon Society,2010(4):1312-1315. |
[9] | 周颖,邱介山,周杰,郭树才.用富勒烯残余烟灰制备炭分离膜的初步研究[J].新型炭材料,1999(01):42-47. |
[10] | Grieco WJ.;Rainey LC.;Vander Sande JB.;Howard JB. .Fullerenic carbon in combustion-generated soot[J].Carbon: An International Journal Sponsored by the American Carbon Society,2000(4):597-614. |
[11] | Jingsong Huang;Boby Ga. Sumpter;Vincent Meunier;Gleb Yushin;Cristelle Portet;Yury Gogotsi .Curvature effects in carbon nanomaterials: Exohedral versus endohedral supercapacitors[J].Journal of Materials Research,2010(8):1525-1531. |
[12] | C. Portet;G. Yushin;Y. Gogotsi .Effect of Carbon Particle Size on Electrochemical Performance of EDLC[J].Journal of the Electrochemical Society,2008(7):(A)531-536. |
[13] | S. A. M. Silva;J. Perez;R. M. Torresi;C. A. Luengo;E. A. Ticianelli .Surface and electrochemical investigations of a fullerene soot[J].Electrochimica Acta,1999(20):3565-3574. |
[14] | Minato Egashira;Shigeto Okada;Yozo Korai .Toluene-insoluble fraction of fullerene-soot as the electrode of a double-layer capacitor[J].Journal of Power Sources,2005(0):116-120. |
[15] | Shi H .Activated carbons and double layer capacitance[J].Electro-chimica Acta,1996,41(10):1633-1639. |
[16] | Qu D;Shi H .Studies of activated carbons used in double-layer ca-pacitors[J].Journal of Power Sources,1998,74(01):99-107. |
[17] | Bushueva EG;Galkin PS;Okotrub AV;Bulusheva LG;Gavrilov NN;Kuznetsov VL;Moiseekov SI .Double layer supercapacitor properties of onion-like carbon materials[J].Physica status solidi, B. Basic research,2008(10):2296-2299. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%