利用交流脉冲微弧氧化电源在氯化钠和不同浓度硅酸钠电解液中对LY12铝合金进行表面处理,对比研究了样品表面有无预制备膜对微弧氧化起弧及生长过程的影响规律.结果表明:铝合金样品表面形成较高阻抗值的膜层是微弧氧化起弧现象得以发生的必要条件;样品表面获取预制备膜抑制了活性电极放电并为后期电击穿提供一个易"失稳"的界面状态,有利于缩短微弧氧化起弧时间,降低起弧电压,但预制备膜厚度和阻抗值大小对起弧时间和电压影响均较小;样品表面有无预制备膜微弧氧化电压-时间曲线有着相似的变化规律,且预制备膜在后期生长过程中重新参与成膜,在相同能量输出条件下所得陶瓷层厚度明显大于无预制备膜铝合金.
LY12 aluminium alloy was processed by microarc oxidation (MAO) in NaCl and Na_2SiO_3 solutions with different concentrations of Na_2SiO_3 using AC electrical source.The effect of prefab coatings on arc starting and growth during MAO process was reaearched.The results show that a coating with high impedance value formed on the sample surface is a necessary condition for arc starting.The discharge of active electrode is restrained by prefab coating, which offers an unstable interface state for microarc discharge to shortening arc starting time and reducing the voltage.No significant effect of thickness and impedance of prefab coatings on arc starting time and voltage is observed.Whether the prefab coating is prepared on the sarnple surface, the curves of voltage-time during MAO is similar.The prefab coating is concemed with forming ceramic coating, which resulta in a fast growth of ceramic coating under the same energy output.
参考文献
| [1] | LIANG Jun;HU Li-tian;HAO Jing-cheng .Improvement of corrosion properties of microarc oxidation coating on magnesium alloy by optimizing current denaity parameten[J].Applied Surface Science,2007,253:6939-6945. |
| [2] | TIAN Jun;LUO Zhuang-zi;QI Shang-kui et al.Structure and antiwear behavior of micro-are oxidized coatings on aluminum alloy[J].Surface and Coatings Technology,2002,154:1-7. |
| [3] | Verdier S;Boinet M;Maximovitch S et al.Fonnation.atructure and composition of anodic films on AM60 magnesium alloy obtained by DC plasma anodizing[J].Corrosion Science,2005,47:1430-1444. |
| [4] | Kriahniyer A;Ramasubramanian M;Popov B N et al.Electrodeposition & characterizations zinc-nickel-phosphorus alloys[J].Plating and Surface Finishing,1999,86(01):99-103. |
| [5] | 蒋百灵,赵仁兵,梁戈,李均明,袁芳.Na2WO4对铝合金微弧氧化陶瓷层形成过程及耐磨性的影响[J].材料导报,2006(09):155-157. |
| [6] | 陈飞,周海,姚斌,杨英歌,吕俊霞,吕反修.镁合金表面微弧氧化陶瓷层摩擦学性能的研究[J].稀有金属材料与工程,2006(05):806-809. |
| [7] | Writz G P;Bown S D;Kriven W M .Ceramic coatings by anodic spark depoaition[J].Materials and Manufacturing Processes,1991,6(01):87-115. |
| [8] | Wang CX;Zhang D;Jiang YF .Growth process and wear resistance for ceramic coatings formed on Al-Cu-Mg alloy by micro-arc oxidation[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(2):674-678. |
| [9] | XIN Shi-gang;SONG Li-xin;ZHAO Rong-gen et al.Influence of cathodic current on composition,structure and properties of Al_2O_3 coatings on aluminum alloy prepared by micro-are oxidation process[J].Thin Solid Films,2006,515(01):326-3332. |
| [10] | 薛文斌,华铭,施修龄,田华.铸造铝合金微弧氧化膜的生长动力学及耐蚀性能[J].硅酸盐学报,2007(06):731-735. |
| [11] | 朱祖芳.铝合金阳极氧化与表面处理技术[M].北京:化学工业出版社,2004:79-81. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%