分析了自1993年至今国内外文献中报道的α-Fe/R2Fe14B纳米晶稀土永磁薄带的实验数据,研究了稀土含量及硼含量对材料磁性能的影响.结果表明,随稀土含量的增加,纳米晶稀土永磁薄带的矫顽力增加,剩磁趋于减小,稀土含量在8%～9%之间获得最佳的综合磁性能;较高的硼含量有利于获得高矫顽力,但不利于得到高剩磁,硼含量在5%～6%之间为宜.