在室温下成功实现了FeCoV合金A方式的等径弯曲通道变形(equal channel angular pressing,简称ECAP),并研究了变形后的显微组织以及回火处理对FeCoV合金ECAP变形显微组织的影响.结果显示,FeCoV合金经ECAP变形后,形成细小的板条状组织,且尺寸明显减小,由0.40μm减小至90 nm.板条内有位错缠结现象.随着ECAP变形道次的增加,细板条发生断裂.4道次ECAP变形FeCoV合金回火后的组织仍为板条组织,板条内有碳化物颗粒和纳米尺度析出相存在.
参考文献
| [1] | 崔忠忻.金属学与热处理原理[M].哈尔滨:哈尔滨工业大学出版社,1998:225. |
| [2] | Valiev R Z;Korznikov A V;Mulyukov R R .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1993,A168(02):141. |
| [3] | Korchef A;Njah N;Masmoudi J et al.[J].Advances in Engineering Materials,2004,6(08):639. |
| [4] | Furukawa M.;Horita Z.;Nemoto M.;Langdon TG.;Iwahashi Y. .The shearing characteristics associated with equal-channel angular pressing[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(2):328-332. |
| [5] | Nakashima K;Horita Z;Nemoto M et al.[J].Acta Materialia,1998,46(05):1589. |
| [6] | Nakashima K;Horita Z;Nemoto M et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2000,281(01):82. |
| [7] | Iwahashi Y;Wang J;Horita Z et al.[J].Scripta Materialia,1996,35(02):143. |
| [8] | 黄海燕.新型FeCoV磁滞合金的研究[J].金属功能材料,2005(02):1-4. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%