以氨水作催化剂,采用溶胶-凝胶法制备出单分散、粒径约300～500 nm的亚微SiO2粒子.研究了氨水浓度、乙醇用量、正硅酸乙酯/水的体积比及硅烷偶联剂浓度对SiO2粒子粒径、分散度及其表面结构的影响,同时还研究了SiO2胶体粒子的稳定性能和成核生长机理.结果表明:SiO2粒子粒径随氨水浓度的增加,先增大后减小,分散度增大;且随着乙醇用量的增加,粒径减小,分散度下降.硅烷偶联剂的加入使得SiO2胶体粒子表面有机成分增多,疏水性增强,其水乳液在常温下不能长久放置,且硅烷偶联剂浓度愈高,粒子间愈容易发生黏连.
参考文献
| [1] | Gill I.;Ballesteros A. .Encapsulation of biologicals within silicate, siloxane, and hybrid sol-gel polymers: An efficient and generic approach[J].Journal of the American Chemical Society,1998(34):8587-8598. |
| [2] | Zhang JF.;Groeseneken G.;Al-kofahi IS. .Behavior of hot hole stressed SiO2/Si interface at elevated temperature[J].Journal of Applied Physics,1998(2):843-850. |
| [3] | Quan Zhang;Jack Miller .ZrO2/SiO2 mixed oxides as catalysts for alcohol dehydration[J].Applied Catalysis A:General,2001,209:1-6. |
| [4] | Mtraun,Yao E K .Microacropic patterning of orientated mesoscopic silica through guided growth[J].Nature,1997,390:674-675. |
| [5] | Kim S W;Kim M;Lee W Y et al.Fabrication of hollow palladium spheres and their successful application to the recyclable heterogeneous catalyst for suzuki coupling reactions[J].Journal of the American Chemical Society,2002,124:7642-7643. |
| [6] | Stober W;Fink A;Bohn E.Controlled growth of monodispersed silica spheres in the micro size range[J].Journal of Colloid and Interface Science,1968(26):62-69. |
| [7] | 王子忱;王莉伟;赵敬哲 等.沉淀法合成高比表面积超细SiO2[J].无机材料学报,1997,12(03):391-396. |
| [8] | 骆锋,阮建明,万千.微乳液法制备纳米二氧化硅粉末工艺的研究[J].硅酸盐通报,2004(05):48-52. |
| [9] | 殷明志,姚熹,吴小清,汪敏强,张良莹.溶胶-凝胶法制备纳米二氧化硅溶胶和多孔二氧化硅薄膜[J].硅酸盐学报,2002(06):766-770. |
| [10] | 赵丽,余家国,程蓓,赵修建.单分散二氧化硅球形颗粒的制备与形成机理[J].化学学报,2003(04):562-566. |
| [11] | 王金忠,赵岩,张彩碚.单分散球形SiO2形成过程的电导率和粘度变化[J].硅酸盐通报,2003(01):88-91. |
| [12] | 林健 .催化剂对正硅酸乙酯水解-聚合机理的影响[J].无机材料学报,1997,12(03):363-369. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%