用自制的电磁离心铸造机在磁场强度为0.10T,离心转速分别为600、960、1370 r/min条件下制备了高碳高速钢,利用光学显微镜(OM)、扫描电子显微镜(SEM)、能谱分析(EDS)对不同转速下制备的高碳高速钢的一次碳化物和二次碳化物进行了实验研究.结果表明,随着离心转速的提高,铸态组织块状碳化物颗粒逐渐变细小、分布变均匀,弥散；共晶组织中碳化物板条逐渐变短、变细,间距变小；热处理组织中细小的颗粒状碳化物逐渐增多,分布趋于均匀、弥散,且粒度呈现减小的趋势.
参考文献
| [1] | M.A. de Carvalho;R.R. Xavier;C. da Silva Pontes Filho .Microstructure, Mechanical Properties and Wear Resistance of High Speed Steel Rolls for Hot Rolling Mills[J].Iron & Steelmaker,2002(1):27-32. |
| [2] | Corbett R B.Roll quality an overview[A].United States of American,1990:215-226. |
| [3] | 符寒光.铸造高速钢轧辊材质研究进展[J].铸造,2009(10):1016-1020. |
| [4] | M.A. de Carvalho;R.R. Xavier;C. da Silva Pontes Filho .Microstructure, Mechanical Properties and Wear Resistance of High Speed Steel Rolls for Hot Rolling Mills[J].Iron & Steelmaker,2002(1):27-32. |
| [5] | Taku TANAKA;Takayuki KOIE;Masatoshi AYAGAKI .High Speed Steel Type Cold Rolling Mill Roll by Continuous Pouring Process for Cladding[J].NIPPON STEEL TECHNICAL REPORT,2002(86):80-85. |
| [6] | 符寒光;邢建东.高速钢轧辊制造技术[M].北京:冶金工业出版社,2007 |
| [7] | 张伟强.金属电磁凝固原理与技术[M].北京:冶金工业出版社,2004 |
| [8] | 张西鹏,寇国军,吴春京.高速钢轧辊材料的研究进展[J].钢铁研究学报,2007(07):4-8. |
| [9] | 韩至成.电磁冶金技术及装备[M].北京:冶金工业出版社,2008 |
| [10] | 王笑天.金属材料学[M].北京:机械工业出版社,1987 |
| [11] | 郭耕三.高速钢及其热处理[M].北京:机械工业出版社,1985 |
| [12] | 王钦娟 .电磁离心铸造高速钢轧辊组织及性能研究[D].长安大学,2010. |
| [13] | 张西鹏,寇国军,吴春京.高速钢轧辊材料的研究进展[J].钢铁研究学报,2007(07):4-8. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%