Effects of hot plastic deformation on microstructures and tensile properties of AZ91 alloy were investigated. Compared with as-T4 microstructures, the as-extruded samples of AZ91 alloy with fine grains exhibit better strength and ductility due to dynamic recrystallization. The succeeded rotation forging also provides finer grains while the strength in creases, but the elongation decreases. Simultaneously, wrought AZ91 alloy shows more balance properties than as-T4 condition ones. An interesting elongation of 228.5% is attained in the as-extruded AZ91 alloy in spite of the coarse grains with the size of 85 μm. The two-step method enhances the superplastic property of AZ91 alloy. The microstructure is still keep ing the same scale of grains after superplastic testing.
参考文献
| [1] | ELIEZER D.New magnesium alloys for automobile applications[A].Pusan,Korea,2001:175. |
| [2] | Froes F H.How to increase the use of magnesium in aerospace applications[A].Dead Sea, Is rael,2000:43. |
| [3] | Edgar R L.Global overview on demand and applications for magnesium alloys[A].Munich, Germany,2000:3. |
| [4] | FRIEDRICH H;Schumann S.The second age of magnesium-research strategies to bring the automo tive industry's vision to reality[A].Dead Sea, Israel,2000:1. |
| [5] | Kojima Y .Project of the platform science and technology for advanced magnesium alloys[J].Materials Transactions,2002,42(07):1154. |
| [6] | Cole G.USCAR and ENCRA magnesium research in Europe and Northern America[A].Dead Sea, Israel,2000:478. |
| [7] | Tan J C;Tan M.J .Superplasticity in a rolled Mg-3Al-lZn alloy by two-stage deformation method[J].Scripta Materialia,2002,47:101. |
| [8] | Tan JC.;Tan MJ. .Superplasticity and grain boundary sliding characteristics in two stage deformation of Mg-3Al-lZn alloy sheet[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):81-89. |
| [9] | Mabuchi M.;Iwasaki H.;Higashi K.;Ameyama K. .Low temperature superplasticity of AZ91 magnesium alloy with non-equilibrium grain boundaries[J].Acta materialia,1999(7):2047-2057. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%