用X射线粉末衍射法,差热分析法和金相分析法测定了La-Ni-Cr三元系600℃等温截面的相关系.结果表明:此截面由10个单相区、17个两相区和8个三相区组成.在本实验条件下未发现新的三元化合物,没有观察到化合物Cr7Ni3和Cr3Ni2的谱线;化合物La3Ni的谱线是由La和La7Ni3的谱线相叠加;没有观察到LaNi2,而观察到La7Ni16的存在.Ni在Cr中的最大固溶度大约为3at%,Cr在Ni,LaNi5,La2Ni7,LaNi3,La2Ni3,LaNi和La7Ni3中的最大固溶度(at%)分别约为35,20,15,8,9,9和6,Cr在La7Ni16中的固溶度几乎为零.
参考文献
[1] | Liu Jingqi;Geng Ke .The isothermal section of the phase diagram of the La-Ni-Ti ternary system at 673 K[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2000(1/2):121-123. |
[2] | Zhou Huaiying;Zhu Yanguo;Liu Jingqi et al.[J].Journal of Alloys and Compounds,2002,345:167-169. |
[3] | Zhuang Yinghong;Deng Haixia;Liu Jingqi et al.[J].Journal of Alloys and Compounds,2004,363:228-231. |
[4] | Zhou Huaiying;Yao Qingrong;Zhuang Yinghong .[J].Journal of Alloys and Compounds,2004,366:161-164. |
[5] | Pan Y Y;Nash P;Massalski T B.Binary Alloy Phase Diagrams 2nd Edition[M].ASM International:Materials Park OH,1991:2406-2408. |
[6] | Klimyenko A V;Seuntjens J;Miller L L et al.[J].Journal of the Less-Common Metals,1988,144:133-141. |
[7] | Paul-Boncour V;Percheron-Guegan A;Diaf M et al.[J].Journal of THE LESS-COMMON METALS,1987,131:201-208. |
[8] | NASH P.Binary Alloy Phase Diagrams 2nd Edition[M].ASM International:Materials Park OH,1991:1298-1302. |
[9] | William Frank Meclune;Mary E Mrose;Benjiamin Past.Powder Diffraction File[M].New York:International Center for Diffraction Data,1999 |
[10] | William Frank Meclune;Mary E Mrose;Benjiamin Past.Alphabetical Indexes Powder Diffraction File[M].New York:International Center for Diffraction Data,1996:180. |
[11] | Rodney P Elliott.Constitution of Binary Alloys, First Supplement[M].New York: McGraw-Hill Book Company,1965:349. |
[12] | Svechnikov V N;Ivanchenko V G;Kobzenko G F .[J].Diagramm'Sostoyaniya Metallicheskikh Sistem,1981,27:60-62. |
[13] | Villars P.Pearson's Handbook,Crystallographic Data for Intermetallic Phases[M].Ohio:ASM Materials Park,1997 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%