本文用正电子湮没技术(PAT)研究了不同硼含量的单晶和多晶Ni_3Al中硼原子的存在形式。在Ni_3Al合金中加入少量硼(≤1.37%)时,一部分硼原子以间隙方式溶解到基体中,使晶格发生畸变,导致基体中正电子寿命(τ)增长;另一部分硼偏聚到空位型缺陷上,产生“填充效应”,导致平均寿命■和S参数下降。硼量为2.22at.-%时,缺陷态的τ显著增长,■和S参数增大,表明在晶界成晶内析出硼化物,诱发了较多的自由体积较大的缺陷。
The behaviour of B atoms added to mono- and poly-crystalline Ni_3Al alloys has been investigated by positron annihilation technique. If an additive of B less than 1.37 at.-%, some of B atoms solid-dissolved interstitially into matrix and distorted the lattice, thus the lifetime of positron in matrix dilated; the others of them segregated on vacancy-like defects and formed" filling effect", thus the mean lifetime and S parameters decreased. If B added up to 2.22 at.-%, more defects having larger free volume were induced by boride eutectic occurred along grain boundaries and grain interior, thus the positron lifetime in vacancy-like defects, mean lifetime and S parameters increased remarkably.
参考文献
[1] | |
[2] | |
[3] | |
[4] | |
[5] | |
[6] | |
[7] | |
[8] | |
[9] |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%