介绍了由硅酸盐水泥与铝酸盐水泥组成的二元体系,以及掺石膏后三元体系的凝结时间、力学性能、体积变形等,水化硬化机理和应用方面的国内外研究现状,并提出了今后的研究重点.
参考文献
| [1] | Gu Ping;Yan Fu;Xie Ping et al.A study of the hydration and setting behaviour of OPC-HAC pastes[J].Cem ConcrRes,1994,24(04):682. |
| [2] | 王志;宋廷寿;周庆明.混合高铝水泥及其水化反应特点[J].建材新科技,1996(01):1. |
| [3] | 刘光华,张进生.高铝水泥与硅酸盐水泥混合物的耐久性[C].第二届中国国际建筑干混砂浆生产应用技术研讨会论文集,2006:83-88. |
| [4] | 兰明章,郑旭.硅酸盐水泥-高铝水泥-无水石膏复合胶凝体系的实验研究[C].第三届中国国际建筑干混砂浆生产应用技术研讨会论文集,2008:198-202. |
| [5] | 托罗波夫HA;李振夏.水泥化学[M].北京:中国建筑工业出版社,1959 |
| [6] | Czernin W;曾镜鸿.水泥化学与物理性能[M].北京:中国建筑工业出版社,1991 |
| [7] | Robson T D.High alumina cements and concretes[M].London:Contractors Record Ltd,1962 |
| [8] | 袁润章.胶凝材料学[M].武汉:武汉工业大学出版社,1996 |
| [9] | 霍世金 .硅酸盐水泥-铝酸盐水泥-石膏三元复合胶凝材料试验研究[D].西安建筑科技大学,2007. |
| [10] | 黄明城 .普通硅酸盐水泥与铝酸盐水泥混合性能研究[D].上海:同济大学,2008. |
| [11] | 刁桂芝;刘光华.硅酸盐水泥与熔融铝酸钙水泥复合性能研究[J].膨胀剂与膨胀混凝土,2008(01):16. |
| [12] | 王培铭,徐玲琳,张国防.0～20℃硅酸盐水泥的水化性能[J].材料导报,2012(04):114-117. |
| [13] | Gu Ping;James J Beaudoin;Edmond G Quinn et al.Early strength development and hydration of ordinary Portland cement/calcium aluminate cement pastes[J].Adv Cement Based Mater,1997,6(02):53. |
| [14] | Kirca (O);Yaman I (O);Tokyay M.Strength development of calcium aluminate cement-portland cement blends at different temperatures[A].Bracknell:HIS BRE Press,2008:487. |
| [15] | 崔素萍,顾雪慈,王子明,兰明章,贾宝生.石膏种类对硅酸盐水泥性能的影响[J].水泥技术,2005(02):29-32. |
| [16] | 杨志强;楼宗汉;胡国君 .低热水泥中石膏的作用机理研究[J].山东矿业学院学报,1996,15(02):158. |
| [17] | 刘光华,张俊生.高铝水泥及其在化学建材中的应用[C].商品砂浆的研究与应用（首届全国商品砂浆学术会议：论文专辑）,2005:286-292. |
| [18] | 李英丁,张铬,徐迅.硬石膏与高铝水泥掺量对无收缩灌浆料性能的影响[J].新型建筑材料,2009(03):10-12. |
| [19] | Xu Linglin;Wang Peiming;Zhang Guofang .Formation of ettringite in portland cement/calcium aluminate cement/calcium sulfate ternary system hydrates at lower temperatures[J].Construct Build Mater,2012,31:347. |
| [20] | Maier S.Ternary system:Calcium alumina cement-Portland cement-gypsum[A].Bracknell:HIS BRE Press,2008:511. |
| [21] | 黄明城,王培铭,刘宾.石膏品种对硅酸盐水泥与铝酸盐水泥复合体系性能影响[C].第二届全国商品砂浆学术交流会论文汇编,2007:66-72. |
| [22] | Hirano Y;Makida K;Komatsu R.Dimensional change of self-leveling materials developed by mixing aluminous cement,Portland cement and anhydrite[A].Bracknell:HIS BRE Press,2008:533. |
| [23] | Kighelman J;Scrivener K L;Zubriggen R.Kinetics of two types of flooring mortar:PC dominated vs CAC dominated[A].Bracknell:HIS BRE Press,2008:567. |
| [24] | Adam M Neville;Peter John Wainwright.High alumina cement concrete[M].Lancaster:ConstructionPressLtd,1975 |
| [25] | Rao B P;Viswanathan V N.Chemistry of arresting strength retrogression in structural hgh alumina cements[A].Editions Septima,1980:51. |
| [26] | Lxami S;Mandal P K;Ghcsh R.Development of a fast setting high strength cement cornposite[A].Brasil:The American Ceramic Society Inc,1986:357. |
| [27] | Mangabhai R J.Calcium aluminate cement[M].London:IOM Communications Ltd,2001 |
| [28] | 刘成楼.水泥基自流平砂浆的研制[J].中国涂料,2008(08):41-44. |
| [29] | 梅宽杰,李东旭.地面用自流平砂浆的制备及性能[J].材料科学与工程学报,2010(06):890-895,945. |
| [30] | 张琳 .水泥混凝土路面快速修补材料的研究与开发[D].长安大学,2009. |
| [31] | 殷庆立,Loris Amathieu,胡冲,齐怿.铝酸盐水泥在堵漏剂中的应用[J].新型建筑材料,2009(02):78-80. |
| [32] | 吴芳,刘小兵.水泥基无收缩灌浆料试验研究[J].粉煤灰,2010(02):7-10. |
| [33] | 兰明章,王艳兵.不同胶凝体系对干粉砂浆防冻性能的影响[C].第三届中国国际建筑干混砂浆生产应用技术研讨会论文集,2008:258-261. |
| [34] | 杉浦孝三.アルミナセソン トハ门[J].耐火物(日本）,1983(04):35. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%