MgO-C continuous temperature-measuring sensors for liquid steel were made of fused magnesia with different critical particle sizes from 0.5 to 2.0 mm,thus the effects what magnesia＇s particle size affect sensors＇ properties and lifetime were studied.The result shows that the MgO-C continuous temperature-measuring sensor has good aggression resistance to basic tundish powders and meets the requirement for response time of temperature measuring practice in tundish.The sensor＇s service life,which is affected by multi-properties of material and operating environment,reached its maximum when the critical particle size of magnesia was 1.0 mm.The average lifetime of sensors was 43 or 40 h when served for casting SPHC or Q195 steel.
参考文献
| [1] | 谢植,次英,孟红记,张华.基于在线黑体空腔理论的钢水连续测温传感器的研制[J].仪器仪表学报,2005(05):446-448,456. |
| [2] | Kurita S .Thermocouple Protecting Tube[P].American,4135538,1979-01-23. |
| [3] | Kurita S .Thermocouple Protecting Tube[P].American,4216028,1980-08-06. |
| [4] | Nakano M;Mori K;Hiraiwa Y et al.Apparatus for Continuously Measuring Temperature of Molten Metal and Method for Making Same[P].American,4984904,1991-01-15. |
| [5] | Phillippi R M;Greenspan D C;Tokay E .Protective Structure for an Immersion Pyrometer[P].American,4721533,1988-01-26. |
| [6] | Park H K .Refractory Sight Tube for Optical Temperature Measuring Device[P].American,5302027,1994-04-12. |
| [7] | Shia Y;Mori H;Kida O et al.Thermocouple Temperature Sensor and a Method of Measuring the Temperature of Molten Iron[P].American,5181779,1993-01-26. |
| [8] | WANG Kui-han;CUI Chuan-meng .Mo-base Ceramet Protection Tubes for Thermocouples[J].Journal of Northeast University of Technology,1992,13(04):348. |
| [9] | Bannister M K;Swain M V .A Preliminary Investigation of the Corrosion of a Tib2/Bn/Aln Composite During Aluminium Evaporation[J].Ceramics International,1989,15(06):375. |
| [10] | 王玺堂,张保国,张少伟,王周福,熊金松.Al2O3-ZrB2-C复合材料性能研究[J].稀有金属材料与工程,2007(z1):632-634. |
| [11] | John Usher;Keith Ray;Jorg Uhlenbusch .Continuous measurement of liquid steel temperature in the tundish[J].Metallurgical Plant and Technology International,1998(4):124-130. |
| [12] | A.S. Gokce;C. Gurcan;S. Ozgen .The effect of antioxidants on the oxidation behaviour of magnesia-carbon refractory bricks[J].CERAMICS INTERNATIONAL,2008(2):323-330. |
| [13] | ZHANG S;Marriott N J;Lee W E .Thermochemistry and Microstruetures of MgO-C Refractories Containing Various Antioxidants[J].European Ceramic Society,2001,21(08):1037. |
| [14] | Kingery W D .Metal-ceramic Interaction:IV,Absolute Measurement of Metal-Ceramic Interracial Energy and Interracial Adsorption of Silicon From Iron-Silicon Alloys[J].American Ceramic Society,1954,37:42. |
| [15] | Kingery W D .Factors Affecting Thermal Stress Resistance of Ceramic Material[J].American Ceramic Society,1955,38:3. |
| [16] | Hasselman D P H .Approximate Theory of Thermal Stress Resistance of Brittle Ceramic Involving Creep[J].American Ceramic Society,1969,50:454. |
| [17] | Hasselman D P H .Griffith Criterion and Thermal Shock Resistance of Single-Phase Versus Multiphase Brittle Ceramics[J].American Ceramic Society,1969,52:288. |
| [18] | ZHANG P;Seetharaman S .Dissolution of MgO in CaO-FeO- CaF2-SiO2 Slag Under Static Conditions[J].American Ceramic Society,1964,77:970. |
| [19] | LIU L;GUO M;Jones P T et al.In Situ Observation of the Direct and Indirect Dissolution of MgO Particles in CaO-Al2O3- SiO2-Based Slag[J].European Ceramic Society,2007,27(04):1961. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%