用铬酸氧化方法处理聚乙烯(PE)薄膜,得到了表面刻蚀均匀的化学改性薄膜;利用XPS、IR表征了薄膜表面的化学变化,采用SEM、AFM、接触角表征了薄膜表面微观结构和物理性能.制备可化学交联及物理交联成水凝胶的聚乙烯醇(PVA)溶液,与表面刻蚀的PE薄膜复合,得到了PVA水凝胶与PE薄膜的表面复合材料.通过剥离强度测定、SEM观察,表明PVA水凝胶与PE薄膜很好地粘接在一起.
参考文献
| [1] | Ricciardi R;Auriemma F;Gaillet C;De Rosa C;Laupretre F .Investigation of the crystallinity of freeze/thaw poly(vinyl alcohol) hydrogels by different techniques[J].Macromolecules,2004(25):9510-9516. |
| [2] | Rosa Ricciardi;Finizia Auriemma;Claudio De Rosa;Francoise Laupretre .X-ray Diffraction Analysis of Poly(vinyl alcohol)Hydrogels,Obtained by Freezing and Thawing Techniques[J].Macromolecules,2004(5):1921-1927. |
| [3] | 郑凯,何吉宇,陈丹萍,杨荣杰.双螺杆挤出法制备聚乙烯醇水凝胶及其表征[J].高分子材料科学与工程,2006(05):189-192. |
| [4] | Hassan CM.;Peppas NA. .Structure and morphology of freeze/thawed PVA hydrogels[J].Macromolecules,2000(7):2472-2479. |
| [5] | Li YL;Neoh KG;Kang ET .Poly(vinyl alcohol) hydrogel fixation on poly(ethylene terephthalate) surface for biomedical application[J].Polymer: The International Journal for the Science and Technology of Polymers,2004(26):8779-8789. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%