以Ti3SiC2和TiC粉为原料,采用热压烧结方法,在外加应力25 MPa,烧结温度1300 ℃条件下,制备了Ti3SiC2/TiC陶瓷复合材料,并研究了复合材料的高温压缩性能.实验结果表明,复合材料在恒应变速率下出现了明显的屈服现象,并呈现塑性变形特征;复合材料在低于韧脆转变温度时其断裂方式主要是脆性断裂,当变形温度达到韧脆转变温度后,复合材料产生大量塑性变形,同时材料的强度明显降低.
参考文献
| [1] | Barsoum MW.;Elraghy T. .SYNTHESIS AND CHARACTERIZATION OF A REMARKABLE CERAMIC - TI3SIC2[J].Journal of the American Ceramic Society,1996(7):1953-1956. |
| [2] | 石随林;潘伟;罗永明 .[J].稀有金属材料与工程,2002,31(Suppl.1):426. |
| [3] | 昝青峰;汪长安;黄勇 et al.[J].稀有金属材料与工程,2003,32(Suppl.1):217. |
| [4] | Barsoum M W .[J].Prog Solid Sta Chem,2000,28:201. |
| [5] | El-Raghy T;Barsoum M W;Zavaliangos A et al.[J].Journal of the American Ceramic Society,1999,82:2855. |
| [6] | 李敬锋;Matsuki T;Takitani Y et al.[J].稀有材料与工程,2002,31(Suppl.1):125. |
| [7] | Tang K;Wang C A et al.[J].Journal of Alloys and Compounds,2001,329:136. |
| [8] | Li J F;Pan W;Sato F et al.[J].Acta Materialia,2001,49(06):937. |
| [9] | Zhou Y C;Sun Z M .[J].Materials Research Innovations,1999,3:171. |
| [10] | Williams W S;Schaal R D .[J].Journal of Applied Physics,1962,33(03):955. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%