研究了不同挥发速率下厚度较薄的凹液层胶体悬浮液的干燥花样。Panasonic照相机用于拍摄宏观干燥花样。结果表明,随着挥发速率的减小,马兰哥尼对流强度下降,胶体悬浮液的干燥花样更为平整均匀。在较低的挥发速率下可避免宽环花样形成,制备得到表面平整的薄膜,反射光谱证明其可作为三维光子晶体材料。
We studyed the effect of evaporation rate on the drying pattern of thin concave layer colloidal suspension.Panasonic camera was used to capture macroscopic pattern.It is shown that with the decrease of evaporation rate,Marangoni convection strength descends,more uniformed drying pattern is obtained.Broad-ring pattern can be avoided and homogeneous film is prepared at lower evaporation rate,and reflection spectrum shows the film can be three-dimensional photonic crystal material.
参考文献
| [1] | 刘立营,王秀峰,章春香,程冰.光子晶体用二氧化硅胶体球的改性制备及其自组装[J].功能材料,2008(12):1953-1955,1958. |
| [2] | Denkov N D;Velev O D;Kralchevsky P A et al.Mech- anism of formation of two dimensional crystals from latex particles on substrates[J].Langmuir,1992,8(12):3183-3190. |
| [3] | Tsuneo Okubo .Convectional,sedimentation,and drying dissipative structures of ethanol suspension of colloidal silica(110 nm in diameter)spheres[J].Colloid and polymer science,2006(2):225-231. |
| [4] | Kimura K;Kanayama S;Tsuchida A;Okubo T .Drying dissipative structures of the aqueous solution of sodium n-alkyl sulfates on a cover glass[J].Colloid and polymer science,2005(8):898-904. |
| [5] | Tsuneo Okubo;Tomio Yamada;Keisuke Kimura;Akira Tsuchida .Drying dissipative structures of aqueous solution of poly (ethylene glycol)on a cover glass[J].Colloid and polymer science,2006(4):396-404. |
| [6] | Tsuneo Okubo .Sedimentation and drying dissipative structures of green tea[J].Colloid and polymer science,2006(3):331-337. |
| [7] | Tsuneo Okubo;Emi Itoh;Akira Tsuchida .Drying dissipative structures of the thermosensitive gels of poly(N-isopropyl acrylamide) on a cover glass[J].Colloid and polymer science,2006(3):339-349. |
| [8] | Hiroshi Fudouzi .Fabricating high-quality opal films with uniform structure over a large area[J].Journal of Colloid and Interface Science,2004(1):277-283. |
| [9] | Teh LK;Tan NK;Wong CC;Li S .Growth imperfections in three-dimensional colloidal self-assembly[J].Applied physics, A. Materials science & processing,2005(7):1399-1404. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%