Influence of Additive Silica on the Laser Melting of the Ceramic Coatings

材料科学技术（英文）, 2003, 19(1): 33-36.

^1, , ^2, , ^3, , ^4, , ^5, , ^6, , ^7, , ^8,

1.Faculty of Material and Energy, Guangdong University of Technology, Guangzhou 510643, China

2.Faculty of Material and Energy, Guangdong University of Technology, Guangzhou 510643, China

3.Faculty of Material and Energy, Guangdong University of Technology, Guangzhou 510643, China

4.Faculty of Material and Energy, Guangdong University of Technology, Guangzhou 510643, China

5.Dept. of Mechano-Electronic Engineering, South China University of Technology, Guangzhou 510641, China

6.Dept. of Mechano-Electronic Engineering, South China University of Technology, Guangzhou 510641, China

7.Institute of Metal Research, Chinese Academy of sciences, Shenyang 110016, China

8.Institute of Metal Research, Chinese Academy of sciences, Shenyang 110016, China

基金项目: 广东省自然科学基金(Grant No: 970253) This work was supported by Doctoral Foundation of Ministryof Education of China(Grant No: D1-102-072)

Influence of Additive Silica on the Laser Melting of the Ceramic Coatings

Keywords： Plasma spraying

The influence of additive silica on the microstructure of plasma sprayed Al2O3 and Al2O3+13 wt pct TiO2 ceramiccoatings at laser melting has been investigated in this study. At the laser melting, additive silica in Al2O3 ceramiccoating can reduce the stress of cooling shrinkage generated during solidification. Moreover, silica can render finersize of grains of the melting layer and form continuous glassy matter around the grain boundaries so as to reducefurther the cooling stresses and to suppress the formation and spreading of cracks. On the other hand, at the lasermelting, TiO2 reacts with Al2O3 and transforms into TiAl2Os. The latter new phase has great and anisotropiccoefficients of thermal expansion leading to big and asymmetrical stresses and thus to form cracks in the meltinglayer of Al2O3+13 wt pct TiO2 coating. Due to the fact that the influence of additive silica on the suppression of theformation of cracks is rather limited and cannot counterbalance the negative effect of TiAl2O5, thus the melting layerof Al2O3+13 wt pct TiO2 coating doped with 3 wt pct SiO2 cracks also. Nevertheless, TiO2 can greatly developthe wear resistance of the ceramic coating as sprayed or laser melted.

参考文献

[1]	Hanzun CHEN;Zhengyi LIU;Yuzhi ZHUANG .[J].Materials Science Progress,1992,6(06):146.
[2]	V Lopes M L .Escudero and J.M.Bello[J].Materials Science and Engineering,1993,A172:189.
[3]	A H Wang;Z Y Tao;B D Zhu;J.M.Fu X.Y.Ma S.J.Deng，X.D.Cheng .[J].Surface and Coatings Technology,1992,52:141.
[4]	G Y Liang;T T Wong .[J].Surface and Coatings Technology,1997,89:121.
[5]	HanzunCHEN;ZhengyiLIU;Yuzhi ZHUANG .[J].金属学报,1993,29B:358.
[6]	Y Z Yang;Z Y Liu;Y Z Zhuang .[J].Surface and Coatings Technology,1997,89:97.
[7]	R Sivakumar;B L Mordike .[J].Surface Engineering,1988,4:127.
[8]	Y Arata;A Ohmori;C J Li .[J].THIN SOLID FILMS,1988,156:315.
[9]	W D Kingery;H.K.Bowen;D.R.Uhmann.Introduction to Ceramics[M].John Wiley & Sons, Inc , New York,1976:448.
[10]	Yuanzheng YANG;ZhiguoLIU;Zhengyi LIU;YuzhiZHUANG .[J].激光杂志,2000,21(01):46.
[11]	W D Kingery;H.K.Bowen;D.R.Uhmann.Introduction to Ceramics[M].John Wiley & Sons, Inc , New York,1976:594.
[12]	杨元政,刘志国,刘正义.等离子喷涂Al2O3陶瓷涂层激光熔化深度的研究[J].激光技术,2000(05):312.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Influence of Additive Silica on the Laser Melting of the Ceramic Coatings

参考文献