通过[001]取向镍基单晶合金拉伸蠕变期间的组织形貌观察,采用应力应变有限元方法计算出立方γ/γ’两相共格界面的von Mises应力分布,研究了合金在蠕变期间γ’相的定向粗化规律.结果表明,施加拉应力可改变立方γ/γ’两相的应力分布,使不同晶面发生晶格收缩与扩张应变,其中,(001)晶面产生晶格收缩可排斥较大半径的Al、Ti原子,(100)和(010)晶面沿平行于应力轴方向产生晶格扩张应变,可诱捕较大半径的Al、Ti原子,是使其γ’相沿扩张晶格的法线定向生长成为类似筛网层状结构的组织演化规律.并进一步提出蠕变期间发生元素扩散和γ’相定向生长的驱动力.
参考文献
| [1] | Feng H et al.[J].MetallMater TransA,2000,31:585. |
| [2] | Yu Xingfu;Tian Sugui;Du Hongqiang;Yu Huichen;Wang Minggang;Shang Lijuan;Cui Shusen .Microstructure evolution of a pre-compression nickel-base single crystalsuperalloy during tensile creep[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2009(1/2):80-86. |
| [3] | Zhou L;Li S X;Chen C R .[J].Zeitschrift fur Metallkunde,2002,4(93):315. |
| [4] | Tien J K;Copley S M .[J].Metallurgical and Materials Transactions,1971,2:543. |
| [5] | Pollock T M et al.[J].Acta Metallurgica Et Materialia,1994,42(06):1859. |
| [6] | Kuhn H A et al.[J].Acta Metallurgica Et Materialia,1991,39:2783. |
| [7] | Biermann H.;Strehler M. .High-Temperature Measurements of Lattice Parameters and Internal Stresses of a Creep-Deformed Monocrystalline Nickel-Base Superalloy[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1996(4):1003-1014. |
| [8] | 田素贵,张静华,杨洪才,徐永波,胡壮麒.单晶镍基合金拉伸蠕变期间γ′相定向粗化的特征及影响因素[J].航空材料学报,2000(02):1-7. |
| [9] | Tian Sugui et al.[J].Materials Science and Technology,2001,17(06):736. |
| [10] | 沙玉辉 et al.[J].金属学报,1999,36:254. |
| [11] | 周丽,于晓琳.[110]方向作用下单晶镍基高温合金γ'相定向筏化的有限元分析[J].沈阳理工大学学报,2008(05):1-4. |
| [12] | 吴文平,郭雅芳.镍基单晶高温合金定向粗化机制有限元分析[J].北京交通大学学报（自然科学版）,2008(04):67-70. |
| [13] | Tian Sugui et al.[J].Materials Science and Technology,2000,16:451. |
| [14] | Eshelby J D .[J].Prog Solid Mech,1961,2:87. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%