采用Sol-gel法在石英玻璃表面制备了TiO2膜,并经过不同温度焙烧得到不同晶相结构的TiO2膜,同时对膜进行了XRD、UV-Vis紫外-可见吸收光谱、SEM、亲水性的表征和比较.结果表明,TiO2膜在450℃焙烧后转为锐钛矿相结构,而700℃焙烧后则完全转变为金红石相结构.在低强度的紫外光照射下,锐钛矿TiO2膜的亲水性优于金红石和无定型态的TiO2膜;但是当光照强度大于1.0 mW/cm2时,锐钛矿、金红石和无定型TiO2膜的亲水性区别不大,无定型TiO2膜在高强度紫外光照射下表现出良好的亲水性.
参考文献
| [1] | Lawrence .[J].Journal of Physics D:Applied Physics,1999,32:1075. |
| [2] | Onda T;Shibuich S;Tsujii K .[J].Langmuir,1996,12:21. |
| [3] | Ren-De S;Nakajima A et al.[J].Journal of Physical Chemistry B,2001,10:1984. |
| [4] | Wang R;Hashimoto Y;Fujishima A et al.[J].Nature,1997,388(31):431. |
| [5] | Watanabe T;Nakajima A;Wang R et al.[J].Thin Solid Films,1999,351:260. |
| [6] | Wang R;Sakai N;Fujishima A et al.[J].Journal of Physical Chemistry B,1999,103:2188. |
| [7] | Ren-De S;Nakajima A;Fujishima A et al.[J].Journal of Physical Chemistry B,2001,105:1984. |
| [8] | Masahiro M;Nobuo K;Shunichi H .[J].Surface Science,2002,511:401. |
| [9] | Aiguo F;Benjamin J .[J].Materials Science and Engineering A,1998,242:50. |
| [10] | Sakai N;Fujishima A;Watanabe T et al.[J].Journal of Physical Chemistry B,2001,105:3023. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%