研究了气体渗氮层和激光淬火-渗氮层的相组成、微观结构、显微硬度及脆性。结果表明,激光淬火-渗氮白亮层中ε-Fe3N含量由14.74%增至69.45%,而脆硬的ξ-Fe2N含量由79.95%降至25.03%。表层的N含量降低,渗氮层N浓度曲线降低趋势平缓,N的总扩散通量增加,渗氮层厚度增加。激光淬火-渗氮层组织晶粒细小致密,渗碳体分布在条状下贝氏体组织中,硬度高的Cr2N颗粒数目增加,白亮层显微硬度值显著提高,渗氮层脆断的临界压力由气体渗氮层的3 N提高到激光淬火-渗氮层的6 N。
The phase composition,microstructure,micro-hardness and brittleness of gas nitriding layer and laser quenching-nitriding layer have been studied.The results show that the content of ε-Fe3N in bright layer of laser quenching-nitriding layer increases from 14.74% to 69.45%,while the content of crisp and hard ξ-Fe2N drops from 79.95% to 25.03%.The curve of nitrogen concentration in nitriding layer decreases gently with the decrease of the nitrogen content in the surface layer.The total diffusion flux of nitrogen and the thickness of nitriding layer increase.After laser quenching-nitriding,the crystal grain is tiny with cementite distributing in strip lower bainite.The number of high hardness Cr2N particles enchances,which obviously improves the micro-hardness of bright layer.Brittle fracture critical pressure of nitriding layer increases from 3N of gas nitriding layer to 6N of laser quenching-nitriding layer.
参考文献
| [1] | Moller W, Parascandola S, Telbizova T, et al. Surface processes and diffusion mechanisms of ion nitrided of stainless steel and aluminium [J]. Surface and Coatings Technology, 2001, 136 (1-3): 73-79. |
| [2] | Van Ingelgem Y, Vandendaela I, Van den Brock D, et al. Influence of laser surface hardening on the corrosion resistance of martensitic stainless steel [J]. Electrochimica Aeta, 2007, 59(27) : 7796-7801. |
| [3] | 钟敏霖,刘文今.国际激光材料加工研究的主导领域与热点[J].中国激光,2008,35(11):1653-1659. |
| [4] | Peligrad A A, Zhou E, Morton D, et al. Transient temperature behaviour and dynamic process models in laser surface melting of clay tiles [ J ]. Surface and Coatings Technology, 2003, 150(1) : 15-23. |
| [5] | 陈长军,张敏,马红岩,等.BT20钛合金表面渗氧研究[J].功能材料,2008,39(3):437-439. |
| [6] | 卑多慧,吕坚,顾剑锋,等.表面纳米化预处理对低碳钢气体渗氮行为的影响[J].材料热处理学报,2002,23(1):19-24. |
| [7] | 高玉魁.表面形变处理对32Cr3MoVA钢渗氮层组织和性能的影响[J].材料热处理学报,2005,26(1):74-76. |
| [8] | 卢柯,吕坚.一种金属材料表面纳米层的制备方法:中国99122670[P].2003-01-22. |
| [9] | 张洪旺,刘刚,黑祖昆,等.表面机械研磨诱导AIS1304不锈钢表层纳米化I:组织与性能[J].金属学报,2003,39(4):342-345. |
| [10] | 席守谋,张建国,孙晓燕,等.38CrMoAlA钢激光淬火+氮化复合处理[J].中国激光,2004,31(6):761-764. |
| [11] | 王学前,曹惠荣.化合物(ε、γ’)层在渗氮及氮碳共渗中的作用[J].四川工业学院学报,200l,20(3):48-51. |
| [12] | 谢善晓.化学热处理译文集[M].北京:国防工业出版社,1981:22-23. |
| [13] | Tong W P, Hana Z, Wang L M, et al. Low- temperature nitriding of 38CrMoAl steel with a nanostructured surface layer indueed by surface mechanical attrition treatment [J]. Surface and Coatings Technology, 2008, 202(20) ; 4957-4963. |
| [14] | 郭铮匀.钢的氮化[M].北京:国防工业出版社,1979:l68. |
| [15] | 钟杰,郑勇,张一欣.功能梯度Ti(C,N)基金属陶瓷制备技术[J].复合材料学报,2009,26(3):111-115. |
| [16] | 周上祺,侯琼,任勤.38CrMoAl钢离子渗氮微观结构的研究[J].金属热处理,2002,27(10):10-12. |
| [17] | 刘龙飞,戴兰宏,凌中,等.冲击剪切载荷下SiCP/6151Al复合材料变局部化及增强颗粒尺寸效应[J].复合材料学报,2002,19(4):51-55. |
| [18] | Buijnsters J G, Shankar P, Sietsma J, et al. Gas nitriding of chromium in NH3 - H2 atmosphere [J]. Materials Science and Engineering, 2003, 341(1/2): 289-295. |
| [19] | 崔忠圻.金属学与热处理[M].北京:机械工业出版社,1993:286. |
| [20] | 褚作明,陈蕴博,张福成.先进超细化处理技术在钢铁材料中的应用[J].金属热处理,2004,29(I):16-23. |
| [21] | 刘其斌,朱维东,邹龙江,等.宽带激光熔覆WCP/Ni基合金梯度复合涂层组织与摩擦磨损特性[J].复合材料学报,2002,19(6):52-56. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%