The oxidation and hot corrosion behavior of Co-Ni-Cr-Al-Ta-Y coating produced by magnetron sputtering with and without enamel coating has been investigated in air at 900ºC and in molten 75 wt pct NaCl+25 wt pct Na2SO4 at 850ºC. The results show that the enamel coating possesses good hot corrosion resistance in the molten salts, in comparison with the sputtered Co-Ni-Cr-Al-Ta-Y coating. In the hot corrosion test, breakaway corrosion did not occur on the samples with enamel coating and the composition of enamel coating did not significantly change either. The oxidation resistance of the sputtered coating, which offers good adhesion, can be improved by the enamel coating.