首先采用溶胶-凝胶法和喷雾干燥法在云母微粉表面包覆VO25,然后与炭黑混合均匀,通过高温退火还原获得VO2/云母复合粉体.利用XRD、SEM、FT-IR等手段对其进行表征,结果表明,碳热还原法制备的VO2/云母复合粉体相变温度为68℃,滞后温宽为16℃,在波长λ=4.55μm(波数=2200cm-1)的红外光波段,加入5%VO2/云母复合粉体的薄膜相变前后透过率变化为26%.
参考文献
| [1] | Morin F J .[J].Physical Review Letters,1959,3:34-36. |
| [2] | 颜家振,黄婉霞,张月,刘小杰,涂铭旌.不同衬底上VO2薄膜的微观结构和光学性能研究[J].稀有金属材料与工程,2008(05):819-822. |
| [3] | Valmalete J C;Gavarri J R .[J].Solar Energy Materials & Solar Cells,1994,33:135-144. |
| [4] | Suzuki H;Yamaguchi K;Miyazaki H .[J].Computer Science and Technology,2007,67:3487-3490. |
| [5] | Zhang K F;Liu X;Xing Z et al.[J].Materials Letters,2007,61:2644-2647. |
| [6] | Cao C X;Gao Y F;Luo H J et al.[J].Journal of Physical Chemistry C,2008,112(08):18810-18814. |
| [7] | Toshiyuki O;Yasuhiro I;Kenkyu R K et al.[J].Journal of Photopolymer Science and Technology,1997,10:211-216. |
| [8] | Zheng C M;Zhang J L;Luo G B et al.[J].Journal of Materials Science,2000,35:3425-3429. |
| [9] | 傅群,储向峰,林晨,雷德铭,郑臣谋.纳米VO2粉体的制备及性能特征[J].无机材料学报,2004(04):767-771. |
| [10] | 王金星 .[J].铁合金,1998,2:27-29. |
| [11] | 徐灿阳,庞明杰,原晨光,陈志刚,潘颐.还原五氧化二钒制备二氧化钒粉末[J].材料科学与工程学报,2006(02):252-254,262. |
| [12] | Wang, F;Liu, Y;Liu, CY .Molten salt synthesis and localized surface plasmon resonance study of vanadium dioxide nanopowders[J].Journal of Solid State Chemistry,2009(12):3249-3253. |
| [13] | 韩宾,赵青南,杨晓东,赵修建.磁控溅射法制备二氧化钒薄膜及其性能表征[J].稀有金属材料与工程,2009(04):717-721. |
| [14] | Yan J Z;Huang W X;Zhang Y et al.[J].Physica Status Solidia Applications and Materials Science,2008,205:2409-2412. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%