The hip joint femoral head prosthesis was prepared using the Al2O3 material, which was synthesized by high purity alumina micro-powder and Mg- Zr- Y composite additives, the cold manufacturing techniques of lathe turning, grade polishing and the matching size correction of the sintered femoral head were studied. The results showed, after being pressed under 200 MPa cold isostatic pressure and being pre-sintered at 1 150 ℃, the biscuit' s strength can meet the demands of lathe turning; After being grade polished by SiC micro-powder and diamond abrading agent and being size corrected by special instruments, the femoral head prosthesis of Al2O3 ceramic has good surface degree of finish and articulates tightly with femoral handle.
参考文献
| [1] | G Willmann.Ceramics for Joint Replacement:What are the Options for the Next Millennium[A].,2000:891. |
| [2] | S P Li.Special Ceramic Technology[M].武汉:华中科技大学出版社,1990 |
| [3] | L Sedel;D Hannouche;M Hamadouche.Long Term Datas Concerning the Use of Alumina on Alumina Beatings in Total Hip Replacements[A].,2004 |
| [4] | WANG Xin-yu;LI Shi-pu;HE Jian-hua .The Effects of Solid Phase Additives on Sintering Properties of Alumina Bioceramic[J].Journal of Wuhan University of Technology.Materials Science edition,2003(2):23-24. |
| [5] | 王欣宇,李世普,陈晓明,贺建华.Preparation for femur prosthesis of ceramic-metal combination artificial hip joint[J].中国有色金属学会会刊(英文版),2002(06):1135-1137. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%