通过DSC热分析、显微硬度测试、透射电镜分析等研究了预变形对2E12铝合金时效析出过程的影响,结果表明:2E12铝合金表现为双阶段时效硬化特征,预变形降低了合金时效第1阶段硬化效果,提高了合金峰时效硬度,缩短了峰时效时间;随预变形量的增加,合金峰时效硬度增大,峰时效时间提前.增加预变形量使合金中析出的板条状S相更为细小、弥散.预变形引入位错对沉淀析出有利,位错环纯刃型位错为S相析出提供有利位置,促进球状S相形核.预变形产生位错结构有利于I型S相析出,并延缓II型S相析出.
参考文献
| [1] | Wanhill R J H;Gestel G F J Avan .[J].Aluminum:Technology applications and Environment:A Profile of A Modern Metal,1978,54(09):573. |
| [2] | Avramovic-Cingara G;Perovic D D;McQueen H J .[J].Aluminum:Technology applications and Environment:A Profile of A Modern Metal,2000,76(04):313. |
| [3] | Latkowski A .[J].Aluminum:Technology applications and Environment:A Profile of A Modern Metal,1986,62(02):113. |
| [4] | Mcevily A;Clark J B;Bond A P .[J].ASM Trans,1967,60:661. |
| [5] | Yuan S;Jeh J;TsauC .[J].Materials Transactions-Japan Institute of Metals,1999,40:233. |
| [6] | NING Ai-lin,LIU Zhi-yi,ZENG Su-min.Effect of large cold deformation after solution treatment on precipitation characteristic and deformation strengthening of 2024 and 7A04 aluminum alloys[J].中国有色金属学会会刊（英文版）,2006(06):1341-1347. |
| [7] | Bagaryatsky Y A;Dokl Akad .[J].S S S R,1952,87:559. |
| [8] | 杨胜;易丹青;杨守杰.[J].中国有色金属学报,2007(z1):59. |
| [9] | Ringer S p;Hono K;Poimear I J .[J].Applied Surface Sconce,1996,94-95:253. |
| [10] | Ratchev P;Verlinden B;Smet De P .[J].Scripm Materialia,1998,38(08):1195. |
| [11] | Wang S C;Starink M J .[J].Acta Materialia,2007,55:933. |
| [12] | Wilson R N;Forsyth P J E .[J].J lnst Metals,1966,94:8. |
| [13] | 李慧中,张新明,陈明安,周卓平,龚敏如.预变形对2519铝合金组织与力学性能的影响[J].中国有色金属学报,2004(12):1990-1994. |
| [14] | 谷亦杰,陈荣,张永刚,黄正,陈昌麒.预变形对463 K人工时效Al-Cu-Mg合金显微组织的影响[J].中国有色金属学报,2001(z1):31-33. |
| [15] | SenN;West D R F .[J].Journal of the Institute of Metals,1969,97:87. |
| [16] | 冯端.金属物理学[M].北京:科学出版社,1998 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%