采用模压工艺制备不饱和聚酯(UP)树脂/大麻纤维复合材料,研究了105℃下热氧老化600h前后复合材料力学性能的变化;采用傅立叶变换红外光谱仪(FTIR)对老化前后复合材料的结构进行对比分析,并通过SEM技术观察复合材料的断面形貌.结果表明,偶联剂KH570处理对复合材料力学性能的总体改善效果最佳.老化600h后,偶联剂处理复合材料具有的最佳力学性能如拉伸强度、拉伸模量、弯曲强度、弯曲模量及冲击强度分别为19.06MPa、5.78GPa、52.988MPa、1.01GPa和3.881kJ/m2.红外分析显示,偶联剂处理得到的复合材料在老化前后的红外图形变化不明显,有些吸收峰甚至得到了加强.SEM结果表明,老化600h后,偶联剂处理的复合材料中纤维仍能较均匀地分散在树脂基体中,两者间的界面粘结良好.
The unsaturated polyester resin reinforced/hemp fiber composites were formed by compression mold-ing process, the thermo-oxidative aging test was carried out for 600 hours at 105℃. The mechanical properties of different composites before and after aging were studied, and the changes of the structures of different materials through the aging test were investigated by FTIR technology, the morphologies of the fractured surfaces of some com-posites were observed by SEM. The result shows, treating the hemp fiber with silane coupling agent KH570 has the best comprehensive positive effect. The tensile strength, tensile modulus, flexural strength, flexural modulus and impact strength of the KH570 treated composite are correspondingly 19.06MPa, 5.78GPa, 52.988MPa, 1.01GPa and 3.881 kJ/mM2 after aging for 600 hours, which indicate that the composite still has the best mechanical proper-ties. The FTIR spectrum of the KH570 treated composite is almost the same before and after the test, and some ab-sorbances are even strengthened. SEM pictures show that the fibers still dissipate in the matrix of the KH570 treated composite homogeneously after aging for 600 hours.
参考文献
| [1] | 雷文,任超,杨涛,金晓明.碱处理对不饱和聚酯树脂/苎麻布复合材料力学性能及界面形貌的影响[J].玻璃钢-复合材料,2007(05):31-35. |
| [2] | 雷文,袁正扬,任超,余旺旺,杨涛.不饱和聚酯树脂/大麻纤维复合材料紫外老化性能的研究[J].玻璃钢/复合材料,2008(05):18-22,33. |
| [3] | 肖加余,曾竟成,王春奇,梁重云,陈一民,张小静,娄斌武.高性能天然纤维复合材料及其制品研究与开发现状[J].玻璃钢/复合材料,2000(02):38-43. |
| [4] | 杨德旭,张林文.天然纤维复合材料在建筑装饰上的应用[J].纤维复合材料,2005(04):39-43. |
| [5] | 张长安,张一甫,王春齐.苎麻落麻纤维的偶联改性研究[J].玻璃钢/复合材料,2002(05):19-21. |
| [6] | 王俊勃,赵川,高晓丁,郑水蓉,孙曼灵.苎麻纤维增强酚醛复合材料的研究[J].纤维复合材料,2001(01):13-15. |
| [7] | 高志强,马会英.大麻纤维的性能及其应用研究[J].北京纺织,2004(06):30-31,38. |
| [8] | 中国不饱和聚酯树脂行业协会.中国不饱和聚酯树脂行业协会第十一届年会通知[OL].http://www,zgblg,cn/Article/zh/200705/11467,html |
| [9] | V. Tserki;N.E. Zafeiropoulos;F. Simon .A study of the effect of acetylation and propionylation surface treatments on natural fibres[J].Composites, Part A. Applied science and manufacturing,2005(8):1110-1118. |
| [10] | Carmen Albano;Miren Ichazo;Jeanette Gonzalez;Maria Delgado;Rebeca Poleo .Effects of filler treatments on the mechanical and morphological behavior of PP+wood flour and PP+sisal fiber[J].Materials research innovations,2001(5/6):284-293. |
| [11] | Franseico Vilaplana;Amparo Ribes-Greus;Sigbritt Karlsson .Degradation of recycled high-impact polystyrene.Simulation by reprocessing and thermo-oxidation[J].Polymer Degradation and Stability,2006,91:2163-5170. |
| [12] | Laurent M.Matuana;Donatien P.Kamdem .Accelerated Ultraviolet Weathering of PVC/Wood-Flour Composites[J].Polymer engineering and science,2002(8):1657-1666. |
| [13] | Ouajai, S;Shanks, RA .Composition, structure and thermal degradation of hemp cellulose after chemical treatments[J].Polymer Degradation and Stability,2005(2):327-335. |
| [14] | 潘宝风,谭克锋.α-亚麻酸改性不饱和聚酯树脂耐湿热老化性能的研究[J].玻璃钢/复合材料,2005(06):24-26. |
| [15] | 鲁博;张林文;曾竟成.天然纤维复合材料[M].北京:化学工业出版社,2005:19-21. |
| [16] | 陈贻文;李庆宏;黄文亮.有机仪器分析[M].长沙:湖南大学出版社,1999:271. |
| [17] | Franscico Vilaplana;Sigbria Karlsso n;Amparo Ribes-Greus .Changes in the microstrueturc and morphology of high-impact polystyrene subjected to multible processing and thermo-oxidative degradation[J].European Polymer Journal,2007,43:4371-4381. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%