用能量为110 keV剂量分则为1×1014ions/cm2、5×1014ions/cm2、2.5×1015ions/cm2和1.25×1016ions/cm2的质子对聚酰亚胺进行注入改性.摩擦磨损试验表明,质子注入能够提高其耐磨性.但在不同载荷下,其摩擦磨损行为随着注入剂量的变化有所不同.未注入样品的磨痕内存在明显的粘着和划痕,而注入之后,粘着和划痕受到抑制,磨痕变得光滑.
参考文献
| [1] | 贾均红,周惠娣,高生强,周华,陈建敏.聚酰亚胺复合材料的摩擦性能及其机理研究[J].摩擦学学报,2002(04):273-276. |
| [2] | 贾均红,高生强,陈建敏,周惠娣,杨华勇.聚四氟乙烯/碳纤维增强聚酰亚胺复合体系的摩擦学性能[J].材料科学与工程学报,2003(02):183-186. |
| [3] | Cai H.;Yan FY.;Xue QJ.;Liu WM. .Investigation of tribological properties of Al2O3-polyimide nanocomposites[J].Polymer Testing,2003(8):875-882. |
| [4] | Liu W M;Yang S R;Li C L et al.[J].Wear,1996,194:103-106. |
| [5] | 杨生荣;刘维民;李长林 等.[J].摩擦学学报,1996,16(02):180-183. |
| [6] | Cai H;Yan F Y;Xue Q J .[J].Materials Science and Engineering A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2004,364:94-100. |
| [7] | Cai H.;Yan FY.;Xue QJ.;Liu WM. .Investigation of tribological properties of Al2O3-polyimide nanocomposites[J].Polymer Testing,2003(8):875-882. |
| [8] | Mishra R;Tripathy S P;Dwivedi K K et al.[J].Radiation Mesurements,2003,36:719-722. |
| [9] | Guenther M;Gerlach G;Suchaneck G et al.[J].SURFACE AND COATINGS TECHNOLOGY,2002,158～159:108-113. |
| [10] | Sabre K;Eichhorn K J;Simon F et al.[J].Surface and Coatings Technology,2001,139:257-264. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%