利用力学性能测试装置和电化学测试技术研究了东-黄管线在役16Mn钢的力学性能指标和腐蚀行为。给出了在役16Mn钢的部分力学性能参数，腐蚀电位随浸泡时间的变化关系，以及不同浸泡时间后的极化曲线和电化学阻抗谱。结果表明，在役16Mn钢的各项力学性能参数相对于未服役的16Mn钢有不同程度的降低。16Mn钢在东营土壤模拟液中的腐蚀行为比较复杂，腐蚀过程表现为初期发生均匀腐蚀，后期发生局部腐蚀，而且整个腐蚀过程中的腐蚀速度不规律变化。
The corrosion behavior of in-service 16Mn steel for Dong-Huang pipeline in Dongying simulated soil solution was investigated by open circuit potential test,polarization curves and electrochemical impedance spectroscopy.The mechanical properies of in-service 16 Mn steel were characterized as well.The results showed that the yield strength,ultimate tensile strength and Young＇s modulus of in-service 16 Mn steel were reduced by comparing with those of 16 Mn steel before service.According to the electrochemical results,the corrosion process of in-service 16 Mn steel in Dongying simulated soil solution was characterized as general corrosion at the beginning,and localized corrosion occurred after several weeks of immersion.Moreover,there was no obvious mathematical relationship between corrosion rate and immersion time.
参考文献
| [1] | 董玉华,余大涛,张宏.土壤湿度对16Mn钢腐蚀行为的影响[J].石油化工腐蚀与防护,2008(01):16-19. |
| [2] | 翁永基,李相怡.A3钢和16Mn钢在土壤环境中腐蚀行为差异的研究[J].腐蚀科学与防护技术,1996(02):134. |
| [3] | 杨锐鹏,翁永基.X70和16Mn钢土壤腐蚀行为比较I.电位和平均腐蚀速度[J].腐蚀科学与防护技术,2005(03):148-150. |
| [4] | 潘明阳.环氧沥青基在机层对16Mn钢在自然海水中腐蚀疲劳寿命的影响[J].腐蚀科学与防护技术,1998(06):316. |
| [5] | 张中祥,孙冬柏,俞宏英,孟惠民,李辉勤.16Mn钢在模拟油田采出介质中的腐蚀行为研究[J].材料保护,2008(01):13-14,27. |
| [6] | 李明齐,何晓英,蔡铎昌,廖钫.16Mn钢在NaCl薄层液膜下腐蚀的电化学研究[J].吉林化工学院学报,2003(02):64-67. |
| [7] | 蔡晓文,戈磊,陈长风.16Mn低合金钢在H2S环境中的氢损伤性能[J].腐蚀与防护,2010(07):520-522,559. |
| [8] | 张雷,霍飞飞,国大鹏,路民旭.碳钢CO2腐蚀产物膜生长行为研究[J].科学技术与工程,2008(15):4089-4094. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%