测量了不同稀土含最的BFe10-1-1合金在流动海水介质中的腐蚀速率,并采用X射线衍射仪和扫描电子显微镜等手段分析腐蚀产物.结果表明,对于成分相同的BFe10-1-1合金,海水流速越大,腐蚀速率越大;在流动的人工海水中,BFe10-1-1合金腐蚀类型以剥蚀为主,稀土含量为0.04%时合金的耐海水腐蚀性能最好,表面形成一层致密的含稀七相(如CeNi5)的腐蚀产物层,微裂纹较少,与基体结合牢固,能有效地减缓腐蚀速率,提高耐腐蚀性能;当稀土含量过高时,耐腐蚀性能反而降低.
参考文献
| [1] | Allam N K,Ashour E A,Hegazy H S,et al.Effects of benzotriazole on the corrosion of CulONi alloy in sulfidepolluted salt water[J].Corros.Sci.,2005,47:2280. |
| [2] | Colin S,Beche E,Berjoan R,et al.An XPS and AES study of the free corrosion of Cu-,Ni-,Zn-based alloys in synthetic sweat[J].Corros.Sci.,1999,41:1051. |
| [3] | Yuan S J,Pehkonen S O.Surface characterization and corrosion behavior of 70/30 Cu-Ni alloy in pristine and sulfide-containing simulated seawater[J].Corros.Sci.,2007,49:1276. |
| [4] | Qu J E,Guo X P,Chen Z Y.Adsorption behaviorofdode-cylamine on copper-nickel alloy surface in NaCl solutions studied by electrochemical methods and AFM[J].Mater.Chem.Phys.,2005,93:388. |
| [5] | 廖乐杰,何福忠.稀土在铜及铜合金中的作用及其作用效果[J].特种铸造及有色合金,1997,(2):52. |
| [6] | 廖乐杰.稀土添加剂在铜及铜合金中的应用与展望[J].上海有色金属,1998,19(3):132. |
| [7] | Zhang Z F,Lin G Y,Zhang S H,et al.Effects of Ce on microstructure and mechanical properties of pure copper[J].Mater.Sci.Eng.,2007,A457(1-2):313. |
| [8] | 中国腐蚀与防护学会《金属腐蚀手册》编委会.金属腐蚀手册[M].上海:科学技术出版社,1987:65. |
| [9] | 王吉会,姜晓霞,李诗卓.铜合金在3.5% NaCl+S2-溶液中的腐蚀磨损行为[J].中国腐蚀与防护学报,1997,17(2):55. |
| [10] | 魏笔.稀七在白铜冷凝管制备中的应用研究[D].长沙:中南大学,2007:34. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%