研究了微量硼和2 %Nb对铸造Ni50Al20Fe30合金组织及性能的影响。结果表明:微量硼的加入可以改善Ni50Al20Fe30合金的强度与塑性,最佳硼含量为0.02 %~0.05 %;此外,微量硼的加入影响该合金的共晶区,从而明显改变合金的微观组织形态。在硼含量为0.02 %时,该合金主要处于β相(NiAl)与γ相的共晶区,这对合金的室温塑性极为有利。添加2 %Nb可明显提高该合金的压缩屈服强度并改善塑性。在室温、650 ℃和1 000 ℃,该合金的压缩屈服强度分别提高30 %、59 %和36 %。

The effect of minor boron content and 2 %Nb on microstructure and mechanical properties of cast Ni50Al20Fe30 alloy has been investigated. The results show that minor B addition can improve the strength and the ductility of the Ni50Al20Fe30 alloy. The range of 0.02 %~0.05 % B is optimal for the alloy. The minor boron can influence the eutectic zone and microstructure of the alloy. The microstructure of alloy with 0.02 % B mainly consists of fine eutectic β (NiAl) and γ phases. This microstructure is favorable to ductility of the alloy at room temperature. The addition of 2 % Nb can evidently increase the yield strength and improve the ductility. The compressive yield strength of the alloy is increased about 30 %, 59 % and 36 % at room temperature, 650 ℃ and 1 000 ℃ respectively.

参考文献

[1] Vedula K;Pathave V;Aslanidis I.Alloys Based on NiAl for High Temperature Applications[A].Pittsburgh:Materials Research Society,1985:411-421.
[2] Vedula K;Stephens J R.B2 Aluminides for High Temperature Applicationsl[A].Pittsburgh:Materials Research Soci-ety,1987:381-391.
[3] 王淑荷 .B2型NiAl金属间化合物及NiAl基合金[J].宇航材料工艺,1993,23(02):1-12.
[4] Guha S;Munroc P R;Baker L.Improving the Low Tempera-ture Ductility of NiAl[A].Pittsburgh:Materials Re-search Society,1989:633-638.
[5] Ran D .NiAl Alloys for High-Temperature Structural Applica-tion[J].Journal of The Minerals,Metals & Materials Society,1991,43(03):44-49.
[6] 王淑荷;郭建亭;赖万慧 等.NiAl-30 at%Fe合金的高温氧化和热腐蚀行为[J].中国腐蚀与防护学报,1993,13(04):357-365.
[7] 王淑荷;郭建亭;赖万慧 等.NiAl-20 at%Fe合金的高温氧化和热腐蚀行为[J].中国腐蚀与防护学报,1995,15(02):135-140.
[8] Holl R T;Wallace W .Impurities and Trace Elements in Nick-el-Base Superalloys[J].International Metals Reviews,1976,21:1-24.
[9] 陈国胜;伍伯华;周乐澄 等.Nb在铁基高温合金中的作用[J].金属学报,1992,28(09):A385-390.
[10] 王淑荷,郭建亭,赖万慧.制备工艺对NiAl-30Fe-Y合金组织与性能的影响[J].航空学报,1996(01):77.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%