在真空定向凝固炉中采用螺旋选晶法制备了一种镍基单晶高温合金,对其进行标准热处理后在1 070℃时效200,400,600,800 h,然后采用扫描电镜和透射电镜对其组织稳定性进行了研究.结果表明:合金经热处理后,获得规则立方状的γ'相组织;在1 070℃的长期时效过程中,随着时效时间的延长,γ'相合并长大,γ基体通道变宽,时效800 h后,合金基本形成完善的筏形组织;时效200 h后无TCP相析出,时效400 h后枝晶干有少量针状TCP相析出,随着时效时间延长,析出的TCP相增多,并由枝晶干向枝晶间延伸;TCP相主要由铼、钨、钼和钴等元素组成,为σ相,与基体存在的取向关系为[001]σ//[112]γ,(110)σ//(220)γ.
参考文献
| [1] | Sato A;Harada H;Yokokawa T;Murakumo T;Koizumi Y;Kobayashi T;Imai H .The effects of ruthenium on the phase stability of fourth generation Ni-base single crystal superalloys[J].Scripta materialia,2006(9):1679-1684. |
| [2] | 任英磊,金涛,管恒荣,胡壮麒.高温长期时效对镍基单晶高温合金γ′相形貌的影响[J].机械工程材料,2004(03):10-12,15. |
| [3] | M. Aghaie-Khafri;M. Hajjavady .The effect of thermal exposure on the properties of a Ni-base superalloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):388-393. |
| [4] | Hobbs, RA;Zhang, L;Rae, CMF;Tin, S .The effect of ruthenium on the intermediate to high temperature creep response of high refractory content single crystal nickel-base superalloys[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):65-76. |
| [5] | 夏鹏成,禹文芳,于金江,孙晓峰,管恒荣,胡壮麒.长期时效对DZ951合金γ′相的影响[J].材料工程,2007(12):8-11. |
| [6] | 马文有,李树索,乔敏,宫声凯,郑运荣,韩雅芳.热处理对镍基单晶高温合金微观组织和高温持久性能的影响[J].中国有色金属学报,2006(06):937-944. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%