以抚顺东露天油页岩制油残渣为原料,用酸提法制备氧化铝,采用单因素考察法确定了抚顺东露天油页岩残渣提取氧化铝的酸溶反应最佳工艺条件为:煅烧温度850℃,煅烧时间1h,所需原料粒度0.074mm,盐酸浓度为12％,液固比为5∶1,酸溶反应温度100℃,反应时间1.5h,各项工艺指标在最佳工艺条件下,Al2O3浸出率为81.75％;采用均相化学沉淀法由酸溶反应得到的氯化铝滤液制备氧化铝的最佳工艺条件为:反应温度55℃,偏铝酸钠浓度0.4mol/L,乙酸乙酯与铝离子物质的量之比为1.7∶1,反应时间1.5h,表面活性剂的用量为总体系质量的0.3％.采用激光粒度分布仪、X射线衍射仪、X射线荧光光谱仪对所制得的产物氧化铝进行了表征和分析研究.
参考文献
| [1] | Preparation of nano-sized α-Al_2O_3 from oil shale ash[J].Energy,2010(1):45. |
| [2] | 陈巧英,午新威,白永民.中和法制备高纯氧化铝微粉[J].中国粉体技术,2003(04):16-18. |
| [3] | Liu Q;Wang A et al.Synthesis,characterization and catalytic applications of mesoporous γ-alumina from boehmite sol[J].Microporous and Mesoporous Materials,2008,111(1-3):323. |
| [4] | Xu Yingmei;He Demin;Wang Dongmei et al.Influence of calcination temperature on leaching rate of aluminum and iron impurities in oil shale ash[J].Oil Shale,2009,26(02):163. |
| [5] | Arro H;Prikk A;Pihu T .Utilization of semi-coke of Estonian shale oil industry[J].Oil Shale,2002,19(02):117. |
| [6] | 李萍,吴国光,苗真勇,王盘成,赵娜,王志华,孟献梁.油页岩半焦与煤混合燃烧特性研究[J].煤炭转化,2010(01):61-64. |
| [7] | 王军,梁杰,王泽,林伟刚,宋文立.温度对油页岩快速热解特性的影响[J].煤炭转化,2010(01):65-68. |
| [8] | 李勇,薛向欣,冯宗玉,姜涛.用油页岩渣制备白炭黑的工艺[J].过程工程学报,2007(04):751-754. |
| [9] | X.M. Jiang;X.X. Han;Z.G. Cui .Progress and recent utilization trends in combustion of Chinese oil shale[J].Progress in energy and combustion science,2007(6):552-579. |
| [10] | Andres Trikkel;Rein Kuusik;Ants Martins .Utilization of Estonian oil shale semicoke[J].Fuel Processing Technology,2008(8):756-763. |
| [11] | XU YING-MEI;HE DE-MIN;JIANG HUI-MING .CHARACTERIZATION OF OIL SHALE PROCESSING RESIDUES AND SEPARATED PRODUCTS[J].Oil Shale,2009(4):500-512. |
| [12] | Gao Guimei;Zou Haifeng;Gan Shucai et al.Preparation and properties of silica nanoparticles from oil shale ash[J].Powder Technology,2009,191(1-2):47. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%