采用SEM、TEM及显微硬度等方法研究了原始组织为层片状珠光体的共析钢激光冲击处理后的组织演变与硬度变化规律.结果表明:单道次激光冲击即可实现共析钢表层铁素体晶粒超细化,等轴铁素体晶粒尺寸约为0.8 μm;激光冲击产生的冲击波诱发材料表层产生高应变速率的塑性变形,渗碳体层片具有较好的塑性变形能力,冲击波中心区域渗碳体层片球化完全,渗碳体颗粒粒径约为50 nm,而冲击波边缘区域渗碳体层片主要发生弯曲、扭折和断裂;塑性变形导致大量位错的产生使得冲击波中心区域材料表层的硬度相比冲击前提高约20%左右.
参考文献
| [1] | Jean E M;Gerard B .Laser generation of stress waves in metal[J].Surface and Coatings Technology,1995,70(2-3):231-234. |
| [2] | Payre P;Scherpereel X;Berthe L et al.Current trends in laser shock processing[J].Surface Engineering,1998,14(05):377-380. |
| [3] | Charles S. Montross;Tao Wei;Lin Ye .Laser shock processing and its effects on microstructure and properties of metal alloys: a review[J].International Journal of Fatigue,2002(10):1021-1036. |
| [4] | Tang Y X;Zhang Y K;Yu C C .Effect of laser shock processing on the fatigue resistance of aluminum alloy[J].ASME Journal of Engineering Materials and Technology,2000,122(01):104-107. |
| [5] | 孔德军,张永康,鲁金忠,邹世坤.激光冲击处理后Ni基高温合金的性能[J].材料研究学报,2006(05):492-495. |
| [6] | 任旭东,张永康,周建忠,冯爱新,鲁金忠.激光冲击处理对Ti6Al4V力学性能的影响[J].功能材料,2006(11):1781-1783. |
| [7] | 张永康,陈菊芳,许仁军.AM50镁合金激光冲击强化实验研究[J].中国激光,2008(07):1068-1072. |
| [8] | 马壮,李应红,张永康,任旭东,张凌峰.激光冲击处理对304不锈钢力学性能的影响[J].材料热处理学报,2007(03):102-105. |
| [9] | Elsayed-Ali, HE;Rigsbee, JM;Banas, G;Chu, JP .Laser-shock processing effects on surface microstructure and mechanical properties of low carbon steel[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,1999(1-2):260-268. |
| [10] | Hu YX;Yao ZQ;Hu J .3-D FEM simulation of laser shock processing[J].Surface & Coatings Technology,2006(3/4):1426-1435. |
| [11] | 沙桂英,韩恩厚,徐永波,张修丽,刘路.针状铁素体钢的动态应力-应变行为[J].材料研究学报,2005(06):561-566. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%