利用等离子渗氮技术,在不同温度下对3Cr13不锈钢渗氮6 h,研究了渗氮温度对渗氮层组织结构和性能的影响.结果表明:渗氮温度显著影响3Cr13不锈钢表面渗氮层的结构与性能,渗层厚度随着渗氮温度的升高而增加;渗氮温度升高促使表面相由a′N相和ε相逐渐变成CrN相及γ′相;随着渗氮温度的升高表面硬度提高,耐磨性能随之提高;而耐蚀性在低温渗氮(400℃)时比基体略有提高,之后(≥450℃)随着渗氮温度的升高呈下降趋势,且低于基体的.
Based on the plasma nitriding technology, the effect of temperature on the microstructure and properties of plasma nitriding layer of 3Cr13 stainless steel was studied. The results show that temperature significantly affected the structure and performance of the nitrided layer. With the nitriding temperature increasing the layer thickness increased, the surface phases gradually precipitated CrN and γ' from the prime α'N and ε, the surface hardness improved and the wear resistance raised. The corrosion resistance which was lower than that of base decreased with the temperature increasing above 450 ℃ except for the low temperature (400 ℃) condition.
参考文献
| [1] | B. Larisch;U. Brusky;H. -J. Spies .Plasma nitriding of stainless steels at low temperatures[J].Surface & Coatings Technology,1999(0):205-211. |
| [2] | Y. Sun;T. Bell .sliding wear characteristics of low temperature plasma nitrided 316 austenitic stainless steel[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1998(1):34-42. |
| [3] | Wang L.;Xu XL.;Sun JC. .Low pressure plasma arc source ion nitriding compared with glow-discharge plasma nitriding of stainless steel[J].Surface & Coatings Technology,2001(1/3):31-37. |
| [4] | 钟厉,韩西,周上祺,任勤.40Cr钢离子渗氮层ε相转变机理研究[J].热加工工艺,2002(03):1-2,5. |
| [5] | 马力,阎永贵,李小亚.Cl-浓度对CrCoMo不锈钢耐蚀性能的影响[J].腐蚀科学与防护技术,2005(03):172-174. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%