采用自主研发的装置结合离子色谱仪研究了Zn-Al-Mg-RE涂层的自封闭特性,同时通过SEM观察了该涂层腐蚀前后表面腐蚀产物的微观形貌.结果表明:随着腐蚀时间的增加,单位时间氯离子渗透通过Zn-Al-Mg-RE涂层的量不断地降低,超过504 h后,单位时间氯离子渗透通过该涂层的量几乎为零;此时涂层表面被非常致密的腐蚀产物所覆盖.由此说明本文的研究方法能够更直观的证明Zn-Al-Mg-RE金属涂层具有自封闭特性.
参考文献
| [1] | Zeng Z S.Nobuaki Sakoda et al.Structure and corrosion behavior of 316L stainless steel coatings formed by HVAF spraying with and without sealing[J].Surf.Coat.Technol.,2008,203(3-4):284. |
| [2] | Byk T V,Gaevskaya T V,Tsybulskaya L S.Effect of electro deposition conditions on the composition,microstructure,and corrosion resistance of Zn-Ni alloy coatings[J].Surf.Coat.Technol.,2008,202(24):5817. |
| [3] | Hu H L Li N,Zhu Y M.Effect of chromate on the electrochemical behavior of sintered Zn-Al coating in seawater[J].Surf.Coat.Technol.,2008,202(24):5847. |
| [4] | Tachibana K,Morinaga Y.Hot dip fine Zn and Zn-Al alloy double coating for corrosion resistance at coastal area[J].Corros.Sci.,2007,49(1):149. |
| [5] | Vilarigues M,Fernandes J C S.Electrochemical behavior of chromium-implanted magnesium in hydroxide,chloride and sulphate solutions[J].Surf.Coat.Technol.,2008,202(17):4086. |
| [6] | Akbarinezhad E,Rezaei F,Neshati J.Evaluation of a high resistance paint coating with EIS measurements:Effect of high AC perturbations[J].Prog.Org.Coat.,2008:61(1):45. |
| [7] | Martinez I,Andrade C.Application of EIS to cathodically protected steel:Tests in sodium chloride solution and in chloride contaminated concrete[J].Corros.Sci.2008,50(10):2948. |
| [8] | Hamlaoui Y,Pedraza F,Tifouti L.Corrosion monitoring of galvanized coatings through electrochemical impedance spectroscopy[J].Corros.Sci.,2008,50(10):1558. |
| [9] | Liu Y,Xu B S,Zhu Z X,et al.New pattern Zn-Al-Mg-RE coating technics for steel structure sustainable design[J].J.Central South Univ.Technol.,2005,12(2):211. |
| [10] | 刘燕.Zn-Al-Mg-RE粉芯丝材及其涂层自封闭机理的研究[D].北京,装甲兵工程学院,2005,45. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%