目的:研究国产芳纶纤维 DAF-III 表面上浆剂的主要成分及其对复合材料界面性能的影响。方法用丙酮溶剂抽提纤维一定时间,分析对比去除上浆剂前后的纤维和抽提溶液,并制备 DAF-III 增强的聚三唑树脂复合材料,测试复合材料的力学性能。结果国产 DAF-III 芳纶纤维的主体结构是聚酰胺苯并咪唑,表面上浆剂主要组分是脂肪族酯类低聚物。溶剂抽提去除了纤维表面大部分上浆剂,裸露的纤维本体存在制备过程中形成的沿纤维方向的大量沟壑;去除上浆剂后,复合材料的 ILSS 和弯曲强度分别提高了181.2%和56.20%。结论纤维表面上浆剂对纤维以及纤维增强的复合材料力学性能影响显著,纤维与树脂通过机械锚合和氢键作用改善界面粘接。
Objective To investigate the main component of the domestic aramid fiber (DAF-III)sizing agents and its effect on the interfacial properties of composites. Methods The fibers were extracted by acetone for a certain period of time. The extracts and fibers before and after extraction were characterized. The DAF-III reinforced polytriazole (PTA) composites were prepared, and the mechanical properties were tested. Results The results showed that the main molecular structure of domestic DAF-III and surface sizing agent were polyamide benzimidazole and aliphatic ester oligomer, respectively. The majority of the sizing agent was removed and plenty of grooves were formed along the axial direction on the exposed fiber consequently. The mechanical properties (ILSS and flexural strength) of desized fiber reinforced PTA resin composite were increased by 181. 2% and 56. 20% , comparing with those of the virgin sample. Conclusion The sizing agent had a remarkable impact on both fibers and mechanical properties of DAF-III reinforced PTA composite. The fiber interacted with PTA through the mechanical interlocking and hydrogen bond.
参考文献
[1] | 熊佳,黄英,王琦洁.高性能纤维的发展和应用[J].玻璃钢/复合材料,2004(05):49-52. |
[2] | YUAN H,WANG C G,ZHANG S,et al . Effect of Surface Modification on Carbon Fiber and Its Reinforced Phenolic Matrix Composite[J].Applied Surface Science,2012,259 |
[3] | 王云英,孟江燕,陈学斌,白杨.复合材料用碳纤维的表面处理[J].表面技术,2007(03):53-57,60. |
[4] | LEAL A A,DEIZELA J M,MCKNIGHT S H,et al . Interfa-cial Behavior of High Performance Organic Fibers[J].Poly-mer,2009,50(5):1228-1235.,2009. |
[5] | WANG J,CHEN P,LI H,et al . The Analysis of Armos Fi-bers Reinforced Poly(Phthalazinone Ether Sulfone Ketone)Composite Surfaces after Oxygen Plasma Treatment[J].Sur-face & Coatings Technology,2008,202(20):4986-4991.,2008. |
[6] | PENG T,CAIR Q,CHEN C F,et al . Surface Modification of Para-aramid Fiber by Direct Fluorination and Its Effect on the Interface of Aramid/Epoxy Composites[J].Journal of Macromolecular Science,2012,51(3):538-550.,2012. |
[7] | 封彤波,肇研,罗云烽,丁东,段跃新,张佐光.不同上浆剂的国产碳纤维复合材料湿热性能研究[J].材料工程,2009(10):36-40. |
[8] | 贺福,王茂章. 碳纤维及其复合材料[M]. 北京:科学出版社,1997. HE Fu,WANG Mao-zhang. Carbon Fiber and Its Composites [M]. Beijing:Science Press,1997.,1997. |
[9] | 张西萍,张为芹,田艳红,王惠琼.碳纤维用上胶剂的研究[J].纤维复合材料,2001(03):3-4. |
[10] | 席玉松,李艳华,陈秋飞,张国良,李怀京.不同种类碳纤维上浆剂的研究[J].高科技纤维与应用,2011(06):5-8. |
[11] | DAI Z S,SHI F H,ZHANG B Y,et al. Effect of Sizing on Carbon Fiber Surface Properties and Fibers/Epoxy Interfa-cial Adhesion [J]. Applied Surface Science, 2011, 257(15):6980-6985.,2011. |
[12] | YAO L R,LI M,WU Q,et al. Comparison of Sizing Effect of T700 Grade Carbon Fiber on Interfacial Properties of Fiber/BMI and Fiber/Epoxy[J]. Applied Surface Science,2012, 263(15):326-333.,2012. |
[13] | 程平,扈艳红,黄诚,杜磊,黄发荣.碳纤维不同表面处理及其对聚三唑基复合材料界面性能的影响[J].工程塑料应用,2013(03):5-10. |
[14] | WANG X F,WAN L Q,HUANG F R,et al. A New Triazole-maleimide Resin via Azide-alkyne Click Chemistry:Synthe-sis and Characterization [J]. Materials Letters, 2011, 65(2):268-270.,2011. |
[15] | XUE L,WAN L Q,HU Y H,et al . Thermal Stability of a Novel Polytriazoleresin[J].Thermochimica Acta,2006,448(2):147-153.,2006. |
[16] | JIN H,WANG Y Y . Synthesis and Characterization of the Novel Meta-modified Aramid Fibers with Liquid Crystalline Properties[J].Polymer Composites,2012,33(9):1620-1627.,2012. |
[17] | 蔡仁钦,彭涛,王凤德,叶光斗,徐建军.Kevlar 49纤维与芳纶Ⅲ的结构与性能研究[J].合成纤维工业,2010(06):28-31. |
[18] | 宋义斌,朱文苑.芳纶涂敷物及其对芳纶复合材料性能的影响[J].合成纤维,2008(07):14-18. |
[19] | 余锦涛,郭占成,冯婷,支歆.X射线光电子能谱在材料表面研究中的应用[J].表面技术,2014(01):119-124. |
[20] | ZHANG S H,HE G Q,LIANG G Z,et al. Comparison of F-12 Aramid Fiber with Domestic Armid Fiber III on Surface Feature [J]. Applied Surface Science, 2010, 256(7):2104-2109.,2010. |
[21] | 姚明,刘志雷,周建萍,杜楠,江蕾.碳纤维表面接枝纳米SiO2的工艺研究[J].表面技术,2013(03):70-74. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%