研究采用水玻璃为原料,稀氨水为催化剂,通过离子交换制备硅酸溶液、硅粉水解增长粒径、纳滤膜浓缩等步骤制备催化剂级硅溶胶.由正交实验获得较佳工艺条件:浓度5％硅酸溶液150 mL,反应温度为70℃,反应时间为8h,10％的稀氨水加入后体系氨浓度为0.6％.在此条件下,可获得平均粒径20 nm左右,浓度40％的球状催化剂级硅溶胶.
参考文献
| [1] | 段晓娜;孙羊羊;张海红;尚会建;郑学明.硅溶胶的研究进展及应用[J].硅酸盐通报,2014(4):836-840. |
| [2] | 吴丹华;于杰;秦舒浩;何文涛.表面改性纳米硅溶胶的制备与表征[J].现代化工,2012(7):70-73. |
| [3] | M. Tomas;H. Amaveda;L.A. Angurel.Effect of silica sol on the dispersion-gelation process of concentrated silica suspensions for fibre-reinforced ceramic composites[J].Journal of the European Ceramic Society,20134(4):727-736. |
| [4] | Isaline Recloux;Marc Debliquy;Alexandra Baroni;Yoann Paint;Alex Lanzutti;Lorenzo Fedrizzi;Marie-Georges Olivier.Optimization of synthesis parameters of mesoporous silica sol-gel thin films for application on 2024 aluminum alloy substrates[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2013Jul.15(Jul.15):201-210. |
| [5] | 彭云涛;谢大勇;熊继全.硅溶胶结合浇注料的特性及工业应用[J].硅酸盐通报,2013(5):978-981,986. |
| [6] | 马纯超;郑典模.硅溶胶的制备与应用[J].山东化工,2008(5):26-29,34. |
| [7] | 殷馨;戴媛静.硅溶胶的性质、制法及应用[J].化学推进剂与高分子材料,2005(6):27-32,41. |
| [8] | 许念强;顾建祥;罗康;郑松保.大颗粒、高浓度硅溶胶的制备新方法[J].化工进展,2005(8):925-929. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%