钎焊法制备WC复合涂层可以克服热喷涂层的许多缺点,但目前对其在中性NaCl介质中的腐蚀行为研究不多.在碳钢表面真空钎焊制备了WC-Ni复合涂层,采用X射线衍射(XRD)分析了WC-Ni复合涂层表面的物相;通过动电位极化曲线考察了其在3％NaCl溶液中的腐蚀电化学行为;通过场发射扫描电镜(FEGSEM)结合EDX能谱仪观察了不同极化电位处理的涂层的表面形貌和化学组成;采用电感耦合等离子体发射光谱分析了不同极化电位下溶解的金属离子浓度.结果表明:钎焊WC-Ni复合涂层主要是由WC,Ni,NiW,Ni2W4C,Cr3NiB6等物相组成,没有W2C等脆性相;阳极极化曲线上出现2个电流密度平台,分别对应Ni,Cr的氧化物膜的形成和W氧化形成WO3膜层,低电位时主要存在Ni的活性溶解,高电位时同时存在Ni,Cr,W等元素的活性溶解;该涂层耐腐蚀性能较好,硬质相WC的脱落减少,耐磨性提高.
参考文献
| [1] | Bao J;Newkirk J W;Bao S .Wear-resistant WC composite hard coatings by brazing[J].Journal of Materials Engineering and Performanc,2004,13(04):385-388. |
| [2] | Shan-Ping Lu;Oh-Yang Kwon;Yi Guo .Wear behavior of brazed WC/NiCrBSi(Co) composite coatings[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2003(5/6):421-428. |
| [3] | Lu SP.;Kwon OY. .Microstructure and bonding strength of WC reinforced Ni-base alloy brazed composite coating[J].Surface & Coatings Technology,2002(1):40-48. |
| [4] | 张艳,田苗苗,李墨,刘蕾.不同Cr含量的Ni基合金电化学腐蚀行为[J].材料研究学报,2011(06):645-650. |
| [5] | C.M. Fernandes;A.M.R. Senos;M.T. Vieira .Mechanical characterization of composites prepared from WC powders coated with Ni rich binders[J].International Journal of Refractory Metals & Hard Materials,2008(5):491-498. |
| [6] | Pourbaix M.Atlas of electrochemical equilibria in aqueous solutions[M].Houston TX:NACE,1974:7-17. |
| [7] | Human A M;Exner H E .The relationship between electrochemical behaviour and in-service corrosion of WC based cemented carbides[J].International Journal of Refractory Metals and Hard Materials,1997,15(1/3):65-71. |
| [8] | Q. Li;T. C. Lei;W. Z. Chen .Microstructural characterization of WCp reinforced Ni-Cr-B-Si-C composite coatings[J].Surface & Coatings Technology,1999(2/3):285-291. |
| [9] | M. M. Stack;M. T. Mathew;C. Hodge .Micro-abrasion-corrosion interactions of Ni-Cr/WC based coatings: Approaches to construction of tribo-corrosion maps for the abrasion-corrosion synergism[J].Electrochimica Acta,2011(24):8249-8259. |
| [10] | Lekatou A;Zois D;Karantzalis A E et al.Electrochemical behaviour of cermet coatings with a bond coat on Al7075:Pseudopassivity,localized corrosion and galvanic effect considerations in asaline environment[J].Corrosion Science,2010,52(08):2616-2635. |
| [11] | A. Lekatou;D. Zois;D. Grimanelis .Corrosion properties of HVOF cermet coatings with bond coats in an aqueous chloride environment[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2008(16):5700-5705. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%