Hyaluronic acid (HA) was chemically modified by polyethylene glycol. Meanwhile,the dynamic mechanics properties of HA derivative and its viscoelastic changes were measured on 3ARES3 Rheometer (Japan) at 25 ℃. Dried cross-linked films of 10×10 mm2 were immersed in phosphate buffered saline(PBS: pH 7.4) at 37 ℃ with different time periods to measure its water content and in vitro degradation. Moreover, cell cultured solutions, which were in the different cultivation vesse with 1 mg/mL Solution of HA derivative as doing experimental sample for 2 d, 4 d and 7 d, were observed, respectively, by an inverted discrepancy microscope. The cell relative growth rate was analyzed with the SPSS10.0 mathematic statistic software. Based on the above experiments,structure-modified HA derivative can meet the requirements of biomaterials in view of rheological and degradation in vitro and cytotoxicity charactereistics from clinical medical aspect under this experiment conditions.
参考文献
| [1] | Laurent T C;Laurent U B;Fraser J R .The Structure and Function of Hyaluronan:An Overview[J].Immunology and Cell Biology,1996,74:A1-A5. |
| [2] | Kim,BS;Mooney,DJ .Development of biocompatible synthetic extracellular matrices for tissue engineering.[J].Trends in Biotechnology,1998(5):224-230. |
| [3] | 陈景华,樊东辉,徐政,顾其胜.聚乙二醇制备的透明质酸衍生物流变性研究[J].同济大学学报（自然科学版）,2006(01):111-115. |
| [4] | Ambrosio L A;Borzacchiello P A;Netti P A et al.Properties of New Materials:Rheological Study on Hyaluronic Acid and Its Derivative Solutions[J].JMS-Pure and Applied Chemistry,1999,A36(718):991-995. |
| [5] | Wik B H;Wik O.Rheology of Hyaluronan and Its Derivative.The Chemistry,Biology and Medical Applications of Hyaluronan and Its Derivatives[M].London,UK:Portland Press,1998:25-29. |
| [6] | Balazs E A.The Viscoelastic Intercellular Matrix and Control of Cell Function by Hyaluronan[A].London,UK:Portland Press,1998:185-188. |
| [7] | Kenji Tomihata;Yoshito Ikada .Preparation of Cross-linked Hyaluronic Acid Films of Low Water Content[J].Journal of Biomaterials,1997,18(03):189-194. |
| [8] | Tomihata K;Burczak K;Shiraki K.Cross-linking and Biodegradation of Native and Denatured Collagen[A].Washington,DC:American Chemical Society,1994:275-278. |
| [9] | Kobayashi H;Shiraki K;Ikada Y .Toxicity Test of Biodegradable Polymers by Implantation in Rabbit Cornea[J].Journal of Biomedical Materials Research,1992,26:1463-1466. |
| [10] | 李彦林,杨志明,解慧琪,秦廷武,黄富国.生物衍生骨支架材料的体外细胞相容性实验研究[J].中国修复重建外科杂志,2001(04):227-231. |
| [11] | Sung Hsing-wen;Huang Dong-nan;Huang lynnl H et al.In Vitro Evaluation of Cytotoxicity of a Naturally Ouurring Cross-linking Reagent for Biological Tissue Fixation[J].Journal of Biomaterials Science:Polymer Edition,1999,10(01):63-67. |
| [12] | Lv Xiaoying;Kappert HF .New Method of Estimated Cytotocity of Dentistry Materials (MTT experiment)[J].Chinese Journal of Nonnasality Medicine,1995,30(05):337-341. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%