以LaO3、Eu2O3和(NaPO3)6为原料,采用共沉淀法制备了LaP3O9∶ Eu3+荧光粉,并对其发光性能进行了分析.结果表明:该荧光粉的最强吸收峰位于391 nm处；两个发射峰分别位于587 nm和616 nm处,且两峰发光强度相近,说明Eu3+在LaP3O9∶ Eu3+晶体场中处于具有非反演中心对称的格位；与LaPO4∶Eu3荧光粉相比LaP3O9∶ Eu3+发出的红光色饱和度更高；Eu3+在LaP3O9∶ Eu3+晶体荧光粉中的掺杂浓度为8at％时,发光强度最大.
参考文献
| [1] | 吴春芳,王育华.LaPO_4：Eu~（3＋）纳米荧光粉的发光强度影响因素[J].材料研究学报,2011(05):534-538. |
| [2] | Guo CF;Luan L;Ding X;Huang DX .Luminescent properties of SrMg2(PO4)(2): Eu2+, and Mn2+ as a potential[J].Applied physics, A. Materials science & processing,2008(2):327-331. |
| [3] | Zubar E C;Zadneprovskii B I;Efryushina N P et al.Synthesis and Luminescence Examination of β-NaCaPO4:Eu2+,Phosphor Promising for White Light-emitting Diode Applications[J].Russian Journal of Applied Chemistry,2011,84(09):1483-1487. |
| [4] | Ines Hammas,Karima Horchani-Naifer,Mokhtar Férid.Conduction properties of condensed lanthanum phosphates:La(PO3)3 and LaP5O14[J].稀土学报（英文版）,2010(03):321-328. |
| [5] | Buijs M;Blasse G .One-and Three-dimensional Energy Migration in Dimorphic EuP3O9[J].Journal of Luminescence,1988,39:323-334. |
| [6] | Kiliaan H S;van Herwijnen F P;Blasse G .The luminescence of Ce3+-sensitized and Tb3+-activated Gadolinium Metaphosphates (GdP3O9-Ce,Tb)[J].Journal of Solid State Chemistry,1988,74(01):39-46. |
| [7] | 洪广言,高信,刘书珍,王文韵,李有谟.掺铈、钆、铽的三磷酸镧的合成及其光谱[J].发光学报,1994(01):26-32. |
| [8] | 高信;洪广言;刘书珍 .LaP3O9:Ce,Tb磷光体的合成与光谱特性[J].应用化学,1993,10(02):70-72. |
| [9] | Dan Wang;Yuhua Wang;Lingli Wang .UV and Vacuum Ultraviolet Luminescence Properties of LaP_3O_9:Eu~(3+)[J].Journal of the Electrochemical Society,2007(1):J32-J34. |
| [10] | 杨定明 .纳米级稀土发光材料的制备及发光性能研究[D].四川大学,2005. |
| [11] | 郭凤瑜;刘念红 .Ce3+、Tb3+激活的LaBO3的发光性能和能量传递[J].北京大学学报,1990,26(02):191-199. |
| [12] | 张世英,魏坤.纳米晶Y2O3：Eu3+红色荧光体的发光性质研究[J].光谱学与光谱分析,2004(04):407-410. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%