采用单辊法和铜模铸造法制备了Fe75-xMxHf3Y2B20(M=Co,Nb;x=0,4 at%)合金系的非晶薄带和非晶棒样品,并测试了该非晶合金系的差示扫描量热曲线、X射线衍射图谱和软磁性能.结果表明:少量的Nb或Co替代Fe75Hf3Y2B20中的Fe元素,合金的热稳定性和玻璃形成能力可得到明显的提高;其中Fe71Nb4Hf3Y2820的过冷液相区宽度△Tx高达75 K,约化玻璃转变温度Trg为0.58,直径达4 mm,饱和磁感应强度为0.97～1.08 T,该非晶合金同时具有较大的热稳定性、较强的玻璃形成能力和较好的软磁性能.
参考文献
| [1] | Duwez P;Lin S C .[J].Journal of Applied Physics,1967,38:4096. |
| [2] | Inoue A;Shinohara Y;Gook J S .[J].Materials Transactions-Japan Institute of Metals,1995,36(12):1427. |
| [3] | Shen T D;Schwarz R B .[J].Applied Physics Letters,1999,75(01):49. |
| [4] | Bitoh T;Makino A;Inoue A et al.[J].Applied Physics Letters,2006,88(18):182 510. |
| [5] | 陈鼎,陈振华,A.Inoue.富铁Fe-Nd-Al系大块非晶合金的制备及其性能[J].中国有色金属学报,2007(03):406-409. |
| [6] | Long Z L;Shen B L;Shao Y et al.[J].Materials Transactions-Japan Institute of Metals,2006,47(10):2566. |
| [7] | Long Z L;Shao Y;Deng X H et al.[J].INTERMETALLICS,2007,15:1453. |
| [8] | Long Z L;Shao Y;YAe G Q et al.[J].Journal of Alloys and Compounda,2008,462:52. |
| [9] | Inoue A;Shibata T;Zhang T .[J].Materials Transactions-Japan Institute of Metals,1995,36(12):1420. |
| [10] | Wang W H .[J].Progress in Materials Science,2007,52(04):540. |
| [11] | Inoue A;Zhang T;Masumoto T .[J].Journal of Non-Crystalline Solids,1993,156-158:473. |
| [12] | Tumbull D .[J].Contemporary Physics,1969,10(05):473. |
| [13] | Lu Z P;Tan H;Li Y et al.[J].Scripta Materialia,2000,42(07):667. |
| [14] | Z. P. Lu;C. T. Liu .A new glass-forming ability criterion for bulk metallic[J].Acta materialia,2002(13):3501-3512. |
| [15] | Lu Z P;Liu C T .[J].Physical Review Letters,2003,91:115505. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%