为解决 HP345焊瓶钢屈强比超标问题,在通钢 FTSR生产线上,对影响屈强比的主要因素控轧控冷工艺进行试验研究。试验结果表明,提高终轧温度和卷取温度,层流冷却模式采取后段冷却,能够使 HP345焊瓶钢的屈强比由最初的0.81降低至0.76,且各项力学性能满足国标 GB 6653-2008要求。
In order to solve the problem of the over standard yield ratio of HP345 steel,the experiment has studied the TMCP technology in tong gang FTSR production line.The results indicate that increasing the finishing tempera-ture and coiling temperature and using after-stage cooling of laminar cooling mode can reduce the yield ratio of HP345 steel from the initial 0.81 to 0.76.The mechanical properties of the plate can also meet the required of GB 6653-2008.
参考文献
| [1] | 刘社牛,巫宝振,王斌,赵刚毅,陈安洛.控轧控冷工艺对HP345屈强比影响的研究[J].河南冶金,2008(06):8-9,18. |
| [2] | 肖丰强,梁英.HP295焊瓶钢生产实践[J].中国冶金,2008(10):37-39,51. |
| [3] | 张海龙,于红波,王本超,李庆胜.高强度焊接气瓶用钢HP345的开发[J].河北冶金,2012(04):18-20,76. |
| [4] | 梁英,关小军,孙卫华.济钢ASP生产线HP295热轧钢带生产工艺分析[J].山东冶金,2007(04):29-31. |
| [5] | 蓝慧芳,杜林秀,刘彦春,刘相华.控轧控冷工艺对高强度结构钢组织及力学性能的影响[J].东北大学学报（自然科学版）,2009(02):200-204. |
| [6] | 张武彬,柴毅忠,孙文填,胡建平,任崇锐.层流冷却系统对气瓶钢性能的影响研究[J].南方金属,2008(02):38-40. |
| [7] | 王克鲁,鲁世强,李鑫,郑海忠,董显娟.轧后冷制度对低碳贝氏体钢组织及屈强比的影响[J].热加工工艺,2008(16):15-17. |
| [8] | 朱伏先;王国栋;叶永箐 等.温度制度对 HP325 热连轧钢板力学性能的影响[J].钢铁,1992,27(02):28. |
| [9] | 于庆波,孙莹,刘相华,王国栋.热轧后停留时间对带钢屈强比影响的研究[J].钢铁,2006(01):66-70. |
| [10] | 朱伏先,佘广夫,张中平,李鑫,刘相华.冷却工艺对HP295焊瓶钢板屈强比的影响[J].钢铁,2005(08):38-42. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%