以氢氧化钡和二氧化碳气体为原料,采用超临界二氧化碳法,通过添加乙二胺四乙酸(EDTA)并控制其用量,制备出柱状、棒状、椭球状和球状等不同形貌的碳酸钡颗粒.采用TG/SDTA、SEM、XRD和FT-IR等对产品进行分析与表征,结果表明:不同形貌碳酸钡粒子均属于正交晶系.同时对EDTA形貌控制机理进行了初步分析.
参考文献
| [1] | 陈英军,王缓.我国碳酸钡的市场现状和发展方向[J].现代化工,2002(05):53-55. |
| [2] | 张嫦,周小菊.针状碳酸钡的合成工艺研究[J].矿冶工程,2004(01):70-71,76. |
| [3] | Yu S H;HelmutColfen;Xu A W et al.Complex Spherical BaCO3 Superstructures Self-asseembled by a Facile Mineralization Process under Control of Simple Polyelectrolytes[J].Crystal Growth and Design,2004,4(01):33-37. |
| [4] | Chen P C;Cheng G Y;Kou M H.Nucleation and Morphology of Barium Carbonate Crystals in a Sem i-batch Crystallizer[J].Journal of Crystal Growth,2002:237-239. |
| [5] | 李道华;叶向荣;忻新泉 .BaCO3纳米晶的固相反应合成及表征[J].化学研究与应用,1999,11(04):415-418. |
| [6] | 肖宇鹏,赵旭,赵丽娜,吴晓霞,雷洪,任素霞,王子忱.以L-组氨酸为模板仿生合成针状纳米碳酸钙[J].高等学校化学学报,2009(03):530-533. |
| [7] | Yonghong Ni;Haiyan Zhang;Jianming Hong;Lei Zhang;Xianwen Wei .PAM-directed fabrication, shape evolution and formation mechanism of BaCO_3 crystals with higher-order superstructures[J].Journal of Crystal Growth,2008(20):4460-4467. |
| [8] | 张嫦,周小菊.球形碳酸钡粉体的制备及生产实践[J].西南民族大学学报（自然科学版）,2008(01):137-140. |
| [9] | 肖世新,陈建铭,郭锴,陈建峰,郭奋.反应沉淀法制备碳酸钡纳米粉体的研究[J].无机盐工业,2001(05):11-13. |
| [10] | 高远浩,牛和林,陈乾旺.BaCO3单晶纳米线的制备和表征[J].无机化学学报,2003(01):37-40. |
| [11] | 于洺;张玉亭 .乳状液法制备憎液溶胶I.BaCO3均匀粒子的制备[J].物理化学学报,1997,13(01):74-77. |
| [12] | 王丽娜,谢长东,霍冀川,刘树信,雷永林.乙二胺四乙酸对碳酸钡粒子形貌影响的研究[J].人工晶体学报,2010(03):788-792. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%