利用x射线衍射(XRD)和差示扫描量热法(DSC)研究了轧制对Zr65Al7.5Ni10Cu12.5Ag5非晶合金中二十面体准晶相析出的影响.实验发现,经轧制塑性变形合金在随后的加热过程中二十面体准晶相的析出量增加,在变形量ε=70%时达到最大.另外,析出的二十面体准晶相的稳定性随着变形量增大而提高,在ε=70%时达到最大,随后又开始降低.这是由于合金在塑性变形过程中的原子组态发生变化所致.
参考文献
[1] | Shechtman D;Blech I;Gratias D et al.[J].Physical Review Letters,1984,53:1951. |
[2] | Tsai A P;Inoue A;Bizen Y .[J].Acta Metallurgica,1989,37:1443. |
[3] | Holzer J C;Kelton K E .[J].Acta Metallurgica,1991,39:1833. |
[4] | Poon S J;DrehmanA J;Lawless K R .[J].Physical Review Letters,1985,55:2324. |
[5] | Molokanov V V;Chebotnikov V N .[J].Journal of Non-Crystalline Solids,1990,117-118:789. |
[6] | Chen M W;Zhang T;Inoue A et al.[J].Applied Physics Letters,1999,75:1697. |
[7] | Inoue A;Zhang T;Saida J et al.[J].Materials Transactions-Japan Institute of Metals,2000,41:362. |
[8] | Liu L;Chan K C .[J].Journal of Alloys and Compounds,2004,364:146. |
[9] | 闫志杰,李金富,王鸿华,何顺荣,周尧和.Effect of the repeated melting of mother ingot on the stability of icosahedral phase precipitated from Zr-Al-Ni-Cu-Ag glass[J].中国科学E辑(英文版),2003(06):639-644. |
[10] | 同育全,申宝成,甘玉生,闫志杰.铸锭凝固组织对相应非晶合金晶化过程中二十面体准晶相形成动力学的影响[J].物理学报,2005(10):4556-4561. |
[11] | 闫志杰;李金富;周尧和 et al.[J].中国科学e辑,2006,49:655. |
[12] | Chela M W;Dutta J et al.[J].Applied Physics Letters,2001,79:42. |
[13] | Spaepen F .[J].Acta Metallurgica,1977,25:407. |
[14] | Steif P S;Spaepen F;Hutchinson J W .[J].Acta Metallurgy,1982,30:447. |
[15] | 闫志杰,李金富,周尧和,仵彦卿.压痕塑性变形诱导非晶合金的晶化[J].物理学报,2007(02):999-1003. |
[16] | Flores K M;Suh D;Dauskardt R H et al.[J].Journal of Materials Research,2002,17:1153. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%