目的:研究水热时间对TC4钛合金微弧氧化膜合成羟基磷灰石( HA)的影响。方法对TC4钛合金微弧氧化膜进行不同时间的水热合成处理,分析其微观形貌、成分及相结构,观察其在模拟体液中浸泡5周后的形貌及结构变化。结果水热处理提高了微弧氧化膜的Ca/P摩尔比,使非晶态钙磷化合物转化为HA晶体,随着水热时间的延长,HA衍射峰数量增多且强度增加。在模拟体液中浸泡5周后,微弧氧化膜表面仅有微量磷酸钙形成,而如水热合成后再浸泡,氧化膜表面的HA几乎完全转化为磷酸钙。结论水热处理有助于钛合金微弧氧化膜表面合成HA晶体。在8 h内,水热时间越长,氧化膜表面的HA含量越高,模拟体液中浸泡后形成的磷酸钙也越多,与人体的相容性越好。

Objective To study the influence of hydrothermal time on hydroxyapatite ( HA) synthesis of microarc oxidized TC4 alloy. Methods The microarc oxidation ( MAO) coatings on TC4 alloy were treated by different hydrothermal synthesis time. The morphology, composition and phase structure of different coatings were analyzed by SEM, EDS and XRD. Besides, the changes of morphology and phase structure were studied when different MAO coatings were soaked in SBF for 5 weeks. Results Hydrothermal synthesis increased the molar ratio of Ca and P in MAO coating, and changed the amorphous calcium phosphate compounds into HA crystals. The diffraction peak of HA was increased and enhanced continuously with the increasing hydrothermal synthesis time. On-ly a little calcium phosphate was produced when MAO coating was soaked in SBF for 5 weeks, whereas the HA crystals of MAO coating treated by hydrothermal synthesis were almost completely converted to calcium phosphate after 5 weeks soaking in SBF. Conclusion Hydrothermal synthesis was helpful to form HA crystals on microarc oxidized titanium. HA crystals increased when hy-drothermal synthesis time was extended from 0 to 8 h, and then more calcium phosphate was produced on the surface of MAO coa-ting after soaking in SBF, which accordingly had better compatibility with human body.

参考文献

[1] Rack HJ;Qazi JI .Titanium alloys for biomedical applications[J].Materials science & engineering, C. Biomimetic and supramolecular systems,2006(8):1269-1277.
[2] 张玉梅,郭天文,李佐臣.钛及钛合金在口腔科应用的研究方向[J].生物医学工程学杂志,2000(02):206-208,217.
[3] 黄平,憨勇,徐可为.用微弧氧化技术处理医用钛合金表面的研究[J].稀有金属材料与工程,2002(04):308-311.
[4] Yang B;Uchida M;Kim HM;Zhang X;Kokubo T .Preparation of bioactive titanium metal via anodic oxidation treatment.[J].Biomaterials,2004(6):1003-1010.
[5] Han Y.;Hong SH.;Xu KW. .Structure and in vitro bioactivity of titania-based films by micro-arc oxidation[J].Surface & Coatings Technology,2003(2/3):249-258.
[6] 刘亮,郭锋,李鹏飞,娅娅.钛生物种植体表面微弧氧化膜制备的电解液研究[J].表面技术,2009(03):37-40.
[7] 魏大庆,周玉,王亚明,贾德昌.微弧氧化钛合金表面形成含钙磷生物梯度涂层研究[J].稀有金属材料与工程,2008(z1):569-572.
[8] 黄平,徐可为,憨勇.钙、磷在钛表面微弧氧化层中的存在形式及进入机制[J].硅酸盐学报,2004(09):1184-1188.
[9] Yildirim OS;Aksakal B;Celik H;Vangolu Y;Okur A .An investigation of the effects of hydroxyapatite coatings on the fixation strength of cortical screws.[J].Medical engineering and physics,2005(3):221-228.
[10] SONG H J;KIM J W;KOOK M S et al.Fabrication of Hydroxyapatite and TiO2 Nanorods on Microarc Oxidized Titanium Surface Using Hydrothermal Treatment[J].Ap-plied Surface Science,2010,256:7056-7061.
[11] Liu F;Wang FP;Shimizu T;Igarashi K;Zhao LC .Formation of hydroxyapatite on Ti-6Al-4V alloy by microarc oxidation and hydrothermal treatment[J].Surface & Coatings Technology,2005(2/3):220-224.
[12] 张勇,黄平,徐可为,憨勇.溶液钙浓度和水热合成条件对微弧氧化TiO2/羟基磷灰石复合膜层形貌和组成的影响[J].稀有金属材料与工程,2003(12):1007-1010.
[13] 陈柳珠,李卫.水热处理对钛表面羟基磷灰石合成的影响[J].稀有金属材料与工程,2008(03):542-546.
[14] 史兴岭,王庆良,葛世荣.钛合金表面微弧氧化/水热处理复合陶瓷层的性能研究[J].表面技术,2007(06):15-17,21.
[15] Y. Vangolu;A. Alsaran;O. S. Yildirim .Wear properties of micro arc oxidized and hydrothermally treated Ti6Al4V alloy in simulated body fluid[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2011(9/10):2322-2327.
[16] 吴刚强,郎中敏,赫文秀,王正德.沉淀法制备纳米羟基磷灰石结晶动力学研究[J].无机盐工业,2009(07):29-31.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%