In order to improve the high temperature strength of tungsten, 30 vol. Pct ZrC particles were added to the tungsten matrix to form a 30ZrCp/W composite. The tensile properties from 20℃ to 1880℃ of the composite were examined.It was shown that with increasing testing temperature, the nonlinearity of the stress strain curve of 30ZrCp/W composite becames obvious over 1200℃ and the Young's modulus decreases and the elongation increases. The ultimate tensile strength increases at first and then decreases with increasing testing temperature. The maximum strength of 431 Mpa was obtained at 1000℃. The strengthening mechanism at high temperatures is the load transfer to ZrC particles and dislocation strengthening of the tungsten matrix with an effect of grain boundary strengthening.
参考文献
| [1] | S W H Yih;C T Wang.[M].Tungsten,Plenum Press,New York,1979 |
| [2] | W D Klopp;W R Witzke .[J].Journal of the Less-Common Metals,1971,24:424. |
| [3] | A Luo;D L Jacobson .[J].International Journal of Refractory Metals and Hard Materials,1992,11:97. |
| [4] | A Crowson;E S Chen.[J].Journal of The Minerals,Metals & Materials Society,1991(07):27. |
| [5] | ZrCp/W复合材料的组织结构和高温强度[J].中国有色金属学报,1999(01):49. |
| [6] | Guiming Song;Houshan Bai;Yu Zhou;Yujin Wang .[J].Rare Metal Materlals and Engineering,2000,29(02):101. |
| [7] | G M Song;Y Zhou;Y J Wang;T C Lei .[J].Journal of Materials Science Letters,1998,17(20):1739. |
| [8] | A Luo;K S Shin;D L Jacobson .[J].Materials Science and Engineering,1991,A148:219. |
| [9] | A Luo;K S Shin;D L Jacobson .[J].Scripta Metallurgica et Materialia,1991,25:2411. |
| [10] | A Luo;D L Jacobson;K S Shin .[J].Scripta Metallurgica et Materialia,1991,25:1811. |
| [11] | Y J Wang;Y Zhou;G M Song;T Q Lei .[J].Journal of Materials Science and Technology,2001,17(01):31. |
| [12] | A G Lanin;V N Turchin;D N Erin .[J].International Journal of Refractory Metals and Hard Materials,1990,9:154. |
| [13] | N F Mott;F R N Nabarro .[J].Proceedings of The Physical Society,1940,52:86. |
| [14] | G W King .[J].Transactions AIME,1969,245:83. |
| [15] | D Mclean.Grain Boundary in Metals[M].Clarendon Press,Oxford,1957:207. |
| [16] | C Zener .Pirate Communication to C S Smith[J].cited in Trans AIME,1948,175:15. |
| [17] | T Y Kosolapova.Handbook of High Temperature Compounds:Properties,Production,and Application[M].Hemisphere Publication Corporation,New York,1990 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%