研究了19.8T强磁场下Fe-0.47C-2.3Si-3.2Mn中碳硅锰钢在共析点以上较高温度的珠光体等温相变过程.讨论了不同处理条件下所获得的组织形貌特征,并对相变动力学进行了定量、半定量的统计分析.结果表明:相比12 T磁场,19.8T磁场使得磁诱发珠光体(MIP)相变可以在更高的温度发生;珠光体(P)中两相的形成速度不同,两组成相面积分数的比值处于动态变化中,强磁场下铁素体(F)具有快速生长优势,渗碳体(Cem)的形成速度滞后于铁素体;MIP中,随等温温度的升高,粒状珠光体相对于片状具有更大的增量.
参考文献
| [1] | Kakeshita T;Shimizu K;Funada S et al.Composition dependence of magnetic field-induced martensitic transformations in Fe-Ni alloys[J].ACTA METALLURGICA,1985,33(08):1381-1389. |
| [2] | Zhang YD;Esling C;Gong ML;Vincent G;Zhao X;Zuo L .Microstructural features induced by a high magnetic field in a hypereutectoid steel during austenitic decomposition[J].Scripta materialia,2006(11):1897-1900. |
| [3] | R.A. Jaramillo;S.S. Babu;G.M. Ludtka .Effect of 30 T Magnetic Field on Transformations in a Novel Bainitic Steel[J].Scripta materialia,2005(6):461-466. |
| [4] | T.P. Hou;K.M. Wu .Alloy carbide precipitation in tempered 2.25 Cr-Mo steel under high magnetic field[J].Acta materialia,2013(6):2016-2024. |
| [5] | Song JY;Zhang YD;Zhao X;Zuo L .Effects of high magnetic field strength and direction on pearlite formation in Fe-0.12%C steel[J].Journal of Materials Science,2008(18):6105-6108. |
| [6] | T. Garcin;S. Rivoirard;C. Elgoyhen .Experimental evidence and thermodynamics analysis of high magnetic field effects on the austenite to ferrite transformation temperature in Fe-C-Mn alloys[J].Acta materialia,2010(6):2026-2032. |
| [7] | Zhang, X.;Zhang, Y.;Gong, M.;Esling, C.;Zhao, X.;Zuo, L. .Magnetic-field-induced microstructural features in a high carbon steel during diffusional phase transformation[J].Journal of Magnetism and Magnetic Materials,2012(24):4184-4188. |
| [8] | Xiaoling Zhou;Rong Zhou;Pengxiang Zhang;Yehua Jiang;Zeng Li;Hui Zhao .Magnetic field induced pearlite transformation in Fe-0.47C-2.31 Si-3.15Mn steel above the eutectoid temperature[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2009(1/2):42-47. |
| [9] | 周晓玲,周荣,蒋业华,李增.硅锰铸钢磁场等温珠光体相变的热动力学分析[J].材料热处理学报,2007(06):88-93. |
| [10] | 刘雯,周晓玲,张希俊,李增,邱豪.强磁场对硅锰铸钢等温珠光体粒化的影响[J].材料热处理学报,2012(04):50-54. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%