以聚二乙氧基硅氧烷(PDEOS)为原料,通过六甲基二硅氮烷(HMDZ)改性剂对制备的凝胶进行表面改性,并常压干燥得到疏水的SiO2气凝胶.研究了改性剂用量对气凝胶疏水性和结构的影响.疏水气凝胶与水的接触角达120°,常压干燥制备的气凝胶具有典型的气凝胶结构特征,气凝胶颗粒尺寸＜100nm,密度和比表面积分别在140～255kg/m3和480～605m2/g范围内.
参考文献
| [1] | Fricke J;Emmerling A .[J].Journal of Sol-Gel Science and Technology,1998,13:299-303. |
| [2] | 陈龙武;甘礼华.[J].化学通报(印刷版),1997(08):21-27. |
| [3] | 吴志坚.无机气凝胶研究进展[J].材料导报,2001(11):38-40. |
| [4] | 姚连增,李小毛,蔡维理,李远红,牟季美,陈志强,何国良,张立德.SiO2气凝胶的制备与表征[J].硅酸盐学报,1998(03):319-323. |
| [5] | 秦国彤,李文翠,郭树才.气凝胶结构控制[J].功能材料,2000(01):26-28,32. |
| [6] | 魏建东,邓忠生,薛小松,孙琪,杨靖,王珏.亚临界干燥制备疏水SiO2气凝胶[J].无机材料学报,2001(03):545-549. |
| [7] | Land VD.;Teeters DC.;Harris TM. .Processing of low-density silica gel by critical point drying or ambient pressure drying[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2001(1/3):11-17. |
| [8] | Kwon Y G;Choi S Y et al.[J].Journal of Materials Science,2000,35:6075-6078. |
| [9] | 李伟,王霞瑜,张平,黄舸,贺小华.溶胶-凝胶法制备疏水型SiO-2气凝胶[J].材料科学与工程,2002(01):58-60. |
| [10] | 李兴华.密度·浓度测量[M].北京:中国计量出版社,1991 |
| [11] | Rao A;Manish M .[J].Materials Research Bulletin,2002,37:1667-1677. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%