采用溶胶-凝胶法和溶胶-凝胶浸渍法制备了纯的和Gd3+掺杂的纳米TiO2,并利用XRD,电化学, PL光谱和UV-vis漫反射光谱等手段对样品进行了表征.考察了焙烧温度和Gd3+掺杂量对TiO2在紫外光照射下光催化分解水制氢活性的影响.结果发现Gd3+的掺入提高了TiO2光解水制氢活性,并且用溶胶-凝胶浸渍法制备的Gd3+掺杂TiO2光催化剂的活性优于用溶胶-凝胶法制备的光催化剂活性,Gd3+的最佳掺杂量为0.5%(质量分数),催化剂的最佳煅烧温度为500℃.Gd3+的掺入阻止了TiO2由锐钛矿相向金红石相的转变,抑制了晶粒的生长,在紫外区的光吸收能力增强,电子-空穴对的分离效率提高,从而提高了TiO2光催化分解水制氢活性.
参考文献
| [1] | Hoffmann M R;Martin S T;Choi W et al.[J].Chemical Reviews,1995,95:69-96. |
| [2] | O'Regan B;Graetzel M .[J].Nature,1991,353:737-739. |
| [3] | Choi W;Termin A;Hoffmann M R .[J].Physical Chemistry,1994,98(05):13669-13679. |
| [4] | Abe R.;Sayama K.;Arakawa H. .Significant effect of iodide addition on water splitting into H-2 and O-2 over Pt-loaded TiO2 photocatalyst: suppression of backward reaction[J].Chemical Physics Letters,2003(3-4):360-364. |
| [5] | Berko A;Biro T;Solymosi F .[J].Journal of Physical Chemistry B,2000,104:2506-2510. |
| [6] | Xu A W;Gao Y;Liu H Q .[J].Journal of Catalysis,2002,207:151-157. |
| [7] | 侯梅芳,李芳柏,李瑞丰,万洪富,周国逸,谢克昌.钕掺杂提高TiO2光催化活性的机制[J].中国稀土学报,2004(01):75-80. |
| [8] | 杨秋景,徐自力,谢超,薛宝永,杜尧国,张家骅.铕掺杂对纳米TiO2的光催化活性的影响[J].高等学校化学学报,2004(09):1711-1714. |
| [9] | 李慧泉,李越湘,周新木,彭绍琴,吕功煊,李树本.La2O3掺杂TiO2光催化剂的制备和性能[J].分子催化,2004(04):304-309. |
| [10] | 李慧泉,李越湘,周新木,彭绍琴.Sm2O3掺杂TiO2光催化剂的制备和性能[J].催化学报,2004(10):814-818. |
| [11] | 王添辉,李越湘,彭绍琴,吕功煊,李树本.铂修饰的稀土掺杂TiO2的光催化制氢活性[J].化学学报,2005(09):797-801. |
| [12] | 黄雅丽,李旦振,付贤智,王绪绪.原位红外光谱法研究Gd3+掺杂TiO2光催化降解乙烯性能[J].无机化学学报,2004(07):868-872. |
| [13] | Peng SQ;Li YX;Jiang FY;Lu GX;Li SB .Effect of Be2+ doping TiO2 on its photocatalytic activity[J].Chemical Physics Letters,2004(1/3):235-239. |
| [14] | 周武艺,唐绍裘,张世英,周锡荣,万隆.制备不同稀土掺杂的纳米氧化钛光催化剂及其光催化活性[J].硅酸盐学报,2004(10):1203-1208. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%