利用背散射电子衍射技术研究了0.02C-5Mn低碳板条马氏体钢中大角度界面对冲击断口中解理裂纹扩展或断口附近二次解理裂纹扩展的影响,以分析该钢韧性的组织控制单元;依据马氏体变体中理想解理晶面{100}的取向差,比较了板条束界和板条块界改变解理裂纹扩展方向的能力.结果表明:解理裂纹或二次解理裂纹扩展时在原奥氏体晶界、板条束界和大部分的板条块界处都发生了大角度转折;板条块界和板条束界阻碍解理裂纹扩展的能力相近,板条块是控制板条马氏体钢解理断裂和韧脆转变温度的组织单元.
参考文献
| [1] | John William MORRIS, Jr .Comments on the Microstructure and Properties of Ultrafine Grained Steel[J].ISIJ International,2008(8):1063-1070. |
| [2] | J.W. MORRIS;Z. GUO;C. R. KRENN .The Limits of Strength and Toughness in Steel[J].ISIJ International,2001(6):599-611. |
| [3] | 王春芳 .低合金马氏体钢强韧性组织控制单元的研究[D].钢铁研究总院,2008. |
| [4] | Chunfang Wang;Maoqiu Wang;Jie Shi .Effect of microstructural refinement on the toughness of low carbon martensitic steel[J].Scripta materialia,2008(6):492-495. |
| [5] | S. Morito;H. Tanaka;R. Konishi .The morphology and crystallography of lath martensite in Fe-C alloys[J].Acta materialia,2003(6):1789-1799. |
| [6] | Kitahara H;Ueji R;Tsuji N;Minamino Y .Crystallographic features of lath martensite in low-carbon steel[J].Acta materialia,2006(5):1279-1288. |
| [7] | Bevis Hutchinson;Joacim Hagstrom;Oskar Karlsson .Microstructures and hardness of as-quenched martensites (0.1-0.5%C)[J].Acta materialia,2011(14):5845-5858. |
| [8] | 王小勇,潘涛,王华,苏航,李向阳,曹兴忠.Ni-Cr-Mo-B超厚钢板表面低碳回火马氏体组织的韧性研究[J].金属学报,2012(04):401-406. |
| [9] | 由洋,王学敏,尚成嘉.奥氏体化温度对HSLA100高强度低合金钢组织及冲击韧性的影响[J].金属学报,2012(11):1290-1298. |
| [10] | 张小立,庄传晶,吉玲康,冯耀荣,赵文轸,霍春勇,王杰武.高钢级管线钢的有效晶粒尺寸[J].机械工程材料,2007(03):4-8. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%